Disorder trapping in rapidly solidified intermetallic compounds
The congruently melting, single phase, intermetallic compounds β-Ni3Ge and ε-Ni5Ge3 were produced by arc melt. Each was subject to rapid solidification via drop-tube processing. Each compound remained fully single phase β-Ni3Ge/ ε-Ni5Ge3, irrespective of the imposed cooling rate. In the investigatio...