The effects of physiological conditions on the fatigue behaviour of zirconia bioceramic

Ceramic materials are creating much interest for use in orthopaedics as the modular component in hip replacement operations. The bioceramic, 3 mol % yttria-stablised zirconia (3Y-TZP), or biograde zirconia, is currently undergoing clinical trials. As materials used for hip replacements are exposed t...

Full description

Bibliographic Details
Main Author: Hulm, B. J.
Published: Swansea University 1998
Subjects:
612
Online Access:http://ethos.bl.uk/OrderDetails.do?uin=uk.bl.ethos.637342
id ndltd-bl.uk-oai-ethos.bl.uk-637342
record_format oai_dc
spelling ndltd-bl.uk-oai-ethos.bl.uk-6373422015-03-20T05:35:41ZThe effects of physiological conditions on the fatigue behaviour of zirconia bioceramicHulm, B. J.1998Ceramic materials are creating much interest for use in orthopaedics as the modular component in hip replacement operations. The bioceramic, 3 mol % yttria-stablised zirconia (3Y-TZP), or biograde zirconia, is currently undergoing clinical trials. As materials used for hip replacements are exposed to cyclic stresses during gait, it is important to understand the long term performance of the material under cyclic loads. In order to determine the long-term fatigue behaviour of biograde zirconia, it was necessary to perform laboratory tests on prepared specimens of the material. Moreover, the programme sought to determine whether the fatigue life of the material was affected by loading parameters and by exposure to a simulated physiological environment. The fatigue tests involved subjecting disc-shaped specimens of 3Y-TZP in the 'as-fired' condition to cyclic biaxial stresses in a concentric ring apparatus, designed specifically for the research programme. Under the present test conditions, the material underwent a definite cyclic fatigue effect but the behaviour was not affected by loading frequency nor by exposure to a simulated physiological environment. A rise in the fatigue limit was recorded when testing the material at a higher stress ratio. The most detrimental flaws in the 3Y-TZP specimens were those caused by green-machine tearing. The remaining failure-initiating flaws were hole/agglomerate pairs, inclusions and machining/handling flaws. Fatigue crack growth from the pre-existing flaws resulted in accumulated damage until the size of the damaged area was critical for specimen failure. Based on laboratory test data, it would appear unlikely that zirconia bioceramic femoral heads would fail from fatigue during their implantation life, although it is paramount that component testing and/or clinical trials are undertaken to provide conclusive evidence.612Swansea University http://ethos.bl.uk/OrderDetails.do?uin=uk.bl.ethos.637342Electronic Thesis or Dissertation
collection NDLTD
sources NDLTD
topic 612
spellingShingle 612
Hulm, B. J.
The effects of physiological conditions on the fatigue behaviour of zirconia bioceramic
description Ceramic materials are creating much interest for use in orthopaedics as the modular component in hip replacement operations. The bioceramic, 3 mol % yttria-stablised zirconia (3Y-TZP), or biograde zirconia, is currently undergoing clinical trials. As materials used for hip replacements are exposed to cyclic stresses during gait, it is important to understand the long term performance of the material under cyclic loads. In order to determine the long-term fatigue behaviour of biograde zirconia, it was necessary to perform laboratory tests on prepared specimens of the material. Moreover, the programme sought to determine whether the fatigue life of the material was affected by loading parameters and by exposure to a simulated physiological environment. The fatigue tests involved subjecting disc-shaped specimens of 3Y-TZP in the 'as-fired' condition to cyclic biaxial stresses in a concentric ring apparatus, designed specifically for the research programme. Under the present test conditions, the material underwent a definite cyclic fatigue effect but the behaviour was not affected by loading frequency nor by exposure to a simulated physiological environment. A rise in the fatigue limit was recorded when testing the material at a higher stress ratio. The most detrimental flaws in the 3Y-TZP specimens were those caused by green-machine tearing. The remaining failure-initiating flaws were hole/agglomerate pairs, inclusions and machining/handling flaws. Fatigue crack growth from the pre-existing flaws resulted in accumulated damage until the size of the damaged area was critical for specimen failure. Based on laboratory test data, it would appear unlikely that zirconia bioceramic femoral heads would fail from fatigue during their implantation life, although it is paramount that component testing and/or clinical trials are undertaken to provide conclusive evidence.
author Hulm, B. J.
author_facet Hulm, B. J.
author_sort Hulm, B. J.
title The effects of physiological conditions on the fatigue behaviour of zirconia bioceramic
title_short The effects of physiological conditions on the fatigue behaviour of zirconia bioceramic
title_full The effects of physiological conditions on the fatigue behaviour of zirconia bioceramic
title_fullStr The effects of physiological conditions on the fatigue behaviour of zirconia bioceramic
title_full_unstemmed The effects of physiological conditions on the fatigue behaviour of zirconia bioceramic
title_sort effects of physiological conditions on the fatigue behaviour of zirconia bioceramic
publisher Swansea University
publishDate 1998
url http://ethos.bl.uk/OrderDetails.do?uin=uk.bl.ethos.637342
work_keys_str_mv AT hulmbj theeffectsofphysiologicalconditionsonthefatiguebehaviourofzirconiabioceramic
AT hulmbj effectsofphysiologicalconditionsonthefatiguebehaviourofzirconiabioceramic
_version_ 1716793189461917696