| Summary: | abstract: Battery performance has been studied at different temperature, C rate. Different types of batteries have been used. Capacity and impedance are two factors, which are focused in the thesis. To evaluate battery performance and battery conditions, the SOC (state of charge) determination methods have been studied in the thesis. There are two types of batteries divided in three groups: group I. Ni-Cd battery (2V, 8Ah); group II. Lead-acid battery (2V, 8Ah); and group III. Lead-acid battery (2V, 25Ah). The impedance testing is using electrochemical impedance spectroscopy methods. AC impedance method has been used to test different state of charge (100%, 80%, 60%, 40%, 20%). For the corrosion part, the corrosion rate of metal material in the heat transfer fluids has been tested at different temperature. Hastelloys C-276 in eutectic molten salts a mixture of NaCl, KCl and ZnCl2 using potentiodynamic method (swap from ± 30 mV in 0.2 mV.s-1). The lowest corrosion rate of Hastelloy C-276 is 5.51 µm per year at 250 °C. Particularly, the corrosion rate of Hastelloy C-276 jumps up to 53.33 µm per year at 400 °C. === Dissertation/Thesis === M.S.Tech Technology 2013
|
|---|