Degradation mechanisms of barium titanate based thick film capacitors
The electrical characteristics, including degradation, of high K (≅ 500) barium titanate based thick film capacitors were studied. It was found that a gold conductor made from Au metallo-organic paste is not compatible with the porous high K dielectric material. The leakage current of a thick film c...