Constitutive modeling of fiber reinforced cement composites

• Main Author: Boulfiza, Mohamed
• Format: Others
• Language: English
• Published: 2009
• Online Access: http://hdl.handle.net/2429/8580

The role of fibers in the enhancement of the inherently low tensile stress and strain capacities of fiber reinforced cementitious composites (FRC) has been addressed through both the phenomenological, using concepts of continuum damage mechanics, and micromechanical approaches leading to the development of a closing pressure that could be used in a cohesive crack analysis. The observed enhancements in the matrix behavior is assumed to be related to the ability of the material to transfer stress across cracks. In the micromechanics approach, this is modeled by the introduction of a nonlinear closing pressure at the crack lips. Due to the different nature of cracking in the pre-peak and post peak regimes, two different micro-mechanical models of the cohesive pressure have been proposed, one for the strain hardening stage and another for the strain softening regime. This cohesive pressure is subsequently incorporated into a finite element code so that a nonlinear fracture analysis can be carried out. On top of the fact that a direct fracture analysis has been performed to predict the response of some FRC structural elements, a numerical procedure for the homogenization of FRC materials has been proposed. In this latter approach, a link is established between the cracking taking place at the meso-scale and its mechanical characteristics as represented by the Young's modulus. A parametric study has been carried out to investigate the effect of crack patterning and fiber volume fractions on the overall Young's modulus and the thermodynamic force associated with the tensorial damage variable. After showing the usefulness and power of phenomenological continuum damage mechanics (PCDM) in the prediction of FRC materials' response to a stimuli (loading), a combined PCDM – NLFM¹ approach is proposed to model (predict, forecast) the complete response of the composite up to failure. Based on experimental observations, this approach assumes that damage mechanics which predicts a diffused damage is more appropriate in the pre-peak regime whereas, NLFM is more suitable in the post-peak stage where the opening and propagation of a major crack will control the response of the material and not a deformation in a continuum sense as opposed to the pre-cracking zone. Tensile and compressive tests have been carried out for the sole purpose of calibrating the constitutive models proposed and/or developed in this thesis for FRC materials. The suitability of the models in predicting the response of different structural members has been performed by comparing the models' forecasts with experimental results carried out by the author, as well as experimental results from the literature. The different models proposed in this thesis have the possibility to account for the presence of fibers in the matrix, and give fairly good results for both high fiber volume fractions (v[sub f] > 2%) and low fiber volume fractions (v[sub f] < 2%). Use of interface elements in a finite element code has been shown to be a powerful tool in analyzing the behavior of concrete substrate- FRC repair materials by the introduction of a zero thickness layer of interface elements to account for the interface properties which usually control the effectiveness of the repair material. === Applied Science, Faculty of === Civil Engineering, Department of === Graduate