Plasticity of [Beta]'AuZn single crystals
Single crystals of the CsCl type intermetallic compound β’AuZn were prepared and tested in tension over a wide range of temperatures, strain rates and orientations for three compositions, Au-rich (51.0 at.% Au), stoichiometric and Zn-rich (51.0 at. % Zn). Slip surfaces are generally non-crystallogr...