Hydrothermal Synthesis and Characterization of Boehmite/Titania Hybrid Materials on Cotton Fabrics
碩士 === 崑山科技大學 === 材料工程研究所 === 107 === A series of novel boehmite/titania hybrid materials was synthesized from aluminum isopropoxide and titanium-n-butoxide using a hydrothermal synthesis process. Grey cotton fabrics were dyed, and the hybrid materials were combined with the pre-treated cotton fabri...
| Main Authors: | , |
|---|---|
| Other Authors: | |
| Format: | Others |
| Language: | zh-TW |
| Published: |
2019
|
| Online Access: | http://ndltd.ncl.edu.tw/handle/mx5cca |
| Summary: | 碩士 === 崑山科技大學 === 材料工程研究所 === 107 === A series of novel boehmite/titania hybrid materials was synthesized from aluminum isopropoxide and titanium-n-butoxide using a hydrothermal synthesis process. Grey cotton fabrics were dyed, and the hybrid materials were combined with the pre-treated cotton fabrics through a padding-drying-curing process. The structures of the hybrid materials were analyzed using FTIR and 27Al-NMR. Moreover, the bonding structures processed cotton fabrics is evaluated using scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS) analyses. Our data show that the electric conductivity of the processed cotton fabrics improved with higher molar of aluminum isopropoxide and all the processed fabrics had a good water repellent performance.
|
|---|