Passivation and Mechanical Properties of Stainless Steel Parts
碩士 === 國立虎尾科技大學 === 車輛工程系碩士班 === 106 === This experiment, the martensitic based stainless steel was compared after heat treatment, the difference of mechanical properties of both nitrogen accelerated cooling and oil quenching was investigated. Then, the chemically passivated method A-A-A(alkaline-ac...
| Main Authors: | , |
|---|---|
| Other Authors: | |
| Format: | Others |
| Language: | zh-TW |
| Published: |
2018
|
| Online Access: | http://ndltd.ncl.edu.tw/handle/d29bwq |
| Summary: | 碩士 === 國立虎尾科技大學 === 車輛工程系碩士班 === 106 === This experiment, the martensitic based stainless steel was compared after heat treatment, the difference of mechanical properties of both nitrogen accelerated cooling and oil quenching was investigated. Then, the chemically passivated method A-A-A(alkaline-acid-alkaline) was used as the surface processing, to this stainless steel to find the suitable condition of passivation treatment to improve and enhance the corrosion performance.
|
|---|