| Summary: | 碩士 === 桃園創新技術學院 === 材料應用科技研究所 === 101 === Ceramic is a boric acid salt or a mixture of low melting silicates glassy coating, and then add the metal oxide colorant, and by the heat energy to be attached to the metal carcass, also called enamel production methods. Because glass, ceramics, metal objects into the surface of the glaze firing, the artifacts are coated on the surface layer of vitreous, the three components of the coating mixture together for silicates, low-temperature glaze can be melted in the three phases of the between objects on the surface. View from the physical and chemical properties, which, similar to the composition of the glass, in addition to acid and alkali resistance, but is not conductive, insolubility, waterproof, airtight, to cover the thin metal solid surface, they seem to protect membrane as to prevent oxidation.
Thesis sintering of copper metal and stainless steel sheet metal ceramic layer comparative study, based on the industry to provide the kiln temperature, mesh, metal thickness firing time and experience, with Taguchi L16 (45) orthogonal array obtain optimum copper plate and stainless steel sheet metal and low temperature sintering process mix glaze, systematic identify and determine the relationship between post-sintering; further experiments with chemical properties, such as salt spray test of the strength of adhesion, the use of Vickers hardness testing methods. MINITAB software application within the one-way ANOVA analysis to identify the significant process control factors. It can get the best sintered metal and ceramic glaze layer surface structure and elemental composition, in order to establish the optimization of process technology.
|
|---|