Preparation and Properties of PPgMA/MICA Nanocomposite

• Main Authors: Li-Wei Jheng, 鄭立偉
• Other Authors: 林朝慨
• Format: Others
• Language: zh-TW
• Published: 2013
• Online Access: http://ndltd.ncl.edu.tw/handle/47814952213953230471

碩士 === 健行科技大學 === 機械工程所 === 101 === The purpose of this research is to prepare PPgMA composites with Mica from content of 1.5, 3, 4.5 and 6wt%, respectively. We use Kneader to produced composites and investigate the composites disperse thermal properties and mechanical properties by different from Mica content of 1.5, 3, 4.5 and 6wt%, respectively. In thermal properties result shows that the decomposition temperature of PPgMA /Mica at 1.5wt% increase 32℃. The melt Temperature of PPgMA/Mica not obvious promotion. The thermal conductivity increases along with the mica content also increases along with it. In mechanical properties of tensile strength, flexural strength and Impact strength increases along with the mica content also increases along with it. Tensile strength increase 8.1% ,flexural strength increase 18%,Impact strength increase 3.9%. The amount of wear decreases 36% of PPgMA /Mica 4.5wt%. In this research only need the right amount mica content be able to improve the PPgMA properties.