Poly(vinylidene fluoride-co-hexafluoro-propylene ) fiber-perfluoro sulfonate proton exchange composite membrane
碩士 === 元智大學 === 化學工程與材料科學學系 === 100 === Electrospinning technology to prepare the poly(vinylidene fluoride-co-hexafluoro-propylene ) (PVdF-co-HFP) nanofibers, this nanofibers membrane as the support material impregnated with Nafion solution produced Nafion / PVdF-co-HFP fiber proton exchangecomposit...
| Main Authors: | , |
|---|---|
| Other Authors: | |
| Format: | Others |
| Language: | zh-TW |
| Online Access: | http://ndltd.ncl.edu.tw/handle/77828659906505312397 |
| Summary: | 碩士 === 元智大學 === 化學工程與材料科學學系 === 100 === Electrospinning technology to prepare the poly(vinylidene fluoride-co-hexafluoro-propylene ) (PVdF-co-HFP) nanofibers, this nanofibers membrane as the support material impregnated with Nafion solution produced Nafion / PVdF-co-HFP fiber proton exchangecomposite film. This composite membrane production of membrane electrode assembly (MEA) H2/O2 fuel cell testing. The experimental data show that at 80。 C with no back pressure, the anode and cathode catalyst of Pt coating weight of 0.2 mg/cm2 and 0.4 mg/cm2. The maximum power density of up to about 992 mW/cm2. The data show that the composite membranes used in PEMFC has great development potential.
|
|---|