Low temperature synthesis of YAG:Ce phosphors by novel sol-gel method
碩士 === 南台科技大學 === 化學工程與材枓工程系 === 100 === In this research, cerium doped yttrium aluminum garnet (YAG:Ce) powder was successfully synthesized at a low temperature for a short time by novel sol-gel reaction method and used boehmite as the aluminum source. The XRD results shown that the formed powder f...
| Main Authors: | , |
|---|---|
| Other Authors: | |
| Format: | Others |
| Language: | zh-TW |
| Published: |
101
|
| Online Access: | http://ndltd.ncl.edu.tw/handle/33668649758392502157 |
| id |
ndltd-TW-100STUT8063002 |
|---|---|
| record_format |
oai_dc |
| spelling |
ndltd-TW-100STUT80630022016-03-28T04:20:04Z http://ndltd.ncl.edu.tw/handle/33668649758392502157 Low temperature synthesis of YAG:Ce phosphors by novel sol-gel method 以新穎溶膠凝膠法於低溫下合成YAG粉體之研究 LU LI PING 劉力萍 碩士 南台科技大學 化學工程與材枓工程系 100 In this research, cerium doped yttrium aluminum garnet (YAG:Ce) powder was successfully synthesized at a low temperature for a short time by novel sol-gel reaction method and used boehmite as the aluminum source. The XRD results shown that the formed powder formed at 1000℃ for 30 min was pure YAG-phase. The SEM and TEM results shown that the product was about 100 nm in diameter. According to the experiment results, the pure garnet phase with high emission intensity powder was formed at low temperature for a short time. Ming-Ching Hsu Ming-Shyong Tsai 許銘清 蔡明雄 101 學位論文 ; thesis 64 zh-TW |
| collection |
NDLTD |
| language |
zh-TW |
| format |
Others
|
| sources |
NDLTD |
| description |
碩士 === 南台科技大學 === 化學工程與材枓工程系 === 100 === In this research, cerium doped yttrium aluminum garnet (YAG:Ce) powder was successfully synthesized at a low temperature for a short time by novel sol-gel reaction method and used boehmite as the aluminum source. The XRD results shown that the formed powder formed at 1000℃ for 30 min was pure YAG-phase. The SEM and TEM results shown that the product was about 100 nm in diameter. According to the experiment results, the pure garnet phase with high emission intensity powder was formed at low temperature for a short time.
|
| author2 |
Ming-Ching Hsu |
| author_facet |
Ming-Ching Hsu LU LI PING 劉力萍 |
| author |
LU LI PING 劉力萍 |
| spellingShingle |
LU LI PING 劉力萍 Low temperature synthesis of YAG:Ce phosphors by novel sol-gel method |
| author_sort |
LU LI PING |
| title |
Low temperature synthesis of YAG:Ce phosphors by novel sol-gel method |
| title_short |
Low temperature synthesis of YAG:Ce phosphors by novel sol-gel method |
| title_full |
Low temperature synthesis of YAG:Ce phosphors by novel sol-gel method |
| title_fullStr |
Low temperature synthesis of YAG:Ce phosphors by novel sol-gel method |
| title_full_unstemmed |
Low temperature synthesis of YAG:Ce phosphors by novel sol-gel method |
| title_sort |
low temperature synthesis of yag:ce phosphors by novel sol-gel method |
| publishDate |
101 |
| url |
http://ndltd.ncl.edu.tw/handle/33668649758392502157 |
| work_keys_str_mv |
AT luliping lowtemperaturesynthesisofyagcephosphorsbynovelsolgelmethod AT liúlìpíng lowtemperaturesynthesisofyagcephosphorsbynovelsolgelmethod AT luliping yǐxīnyǐngróngjiāoníngjiāofǎyúdīwēnxiàhéchéngyagfěntǐzhīyánjiū AT liúlìpíng yǐxīnyǐngróngjiāoníngjiāofǎyúdīwēnxiàhéchéngyagfěntǐzhīyánjiū |
| _version_ |
1718212317024354304 |