Hot cracking of CF8-Alloy 52M welds
碩士 === 國立臺灣大學 === 材料科學與工程學研究所 === 100 === In this study, the gas tungsten arc welding process was used to perform overlay welding of Alloy 52M (a nickel-based filler metal) onto CF8 stainless steels consisted of either 0.006 wt.% (CF8-L) or 0.14 wt.% (CF8-H) sulfur. While direct depositing Alloy...
Main Authors: | Hsien-An Chu, 朱顯安 |
---|---|
Other Authors: | Chun Chen |
Format: | Others |
Language: | zh-TW |
Published: |
2012
|
Online Access: | http://ndltd.ncl.edu.tw/handle/04875771425144259109 |
Similar Items
-
The Comparison of Cracking Susceptibility of IN52M and IN52MSS Overlay Welds
by: Min-Yi Chen, et al.
Published: (2019-06-01) -
Susceptibility of Hot Cracking in Laser Treated Cladding of Alloy 52
by: Meng-HsiuLee, et al.
Published: (2014) -
Stress Corrosion Cracking Behavior of A508-Alloy 52 and 316L-Alloy 52 Welds under High-temperature Water
by: Wei-Chih Chung, et al.
Published: (2011) -
Effect of Niobium Addition on Solidification Cracking Susceptibility of Alloy 52 by Laser Beam Welding
by: Sheng-WenTseng, et al.
Published: (2018) -
The Study of Weld Hot Cracking of Aluminum Alloys 6061 and 7075
by: Chen Chun Kai, et al.
Published: (2003)