Reactive Phenomenon between Molten Titanium alloy(Ti-6Al-4V) and Al2O3/Y2O3/ZrO2 Composites

碩士 === 國立交通大學 === 材料科學與工程學系 === 100 === Various Al2O3/Y2O3/ZrO2 as sintering samples were reacted with titanium alloy at 1700℃/2h. Analyzing the microstructure of the reaction interface was characterized with XRD and SEM/EDS after reaction. α-Ti(Al、V、O) and TixOy are found in Ti-6Al-4V side after...

Full description

Bibliographic Details
Main Authors: Lee, Hsiang-Yu, 李祥宇
Other Authors: Lin, Chien-Cheng
Format: Others
Language:zh-TW
Published: 2012
Online Access:http://ndltd.ncl.edu.tw/handle/36528734065640141051
Description
Summary:碩士 === 國立交通大學 === 材料科學與工程學系 === 100 === Various Al2O3/Y2O3/ZrO2 as sintering samples were reacted with titanium alloy at 1700℃/2h. Analyzing the microstructure of the reaction interface was characterized with XRD and SEM/EDS after reaction. α-Ti(Al、V、O) and TixOy are found in Ti-6Al-4V side after diffusion reaction for all samples. In ceramic side, each sample have found different phases because each phase have diverse affinity with Ti. Some of the compound have been observed, including Y2O3,α-Ti(Al、V、O), Y-ZrO2, Y4Al2O9, Ti3Al, AlZr2, Al3Zr2, YAlO3, etc.The affinity with Ti of those compound can be fall into rank as Al2O3 > YAG > Y-ZrO2> Y2O3. YAG has play an important role during diffusion process. It will be necessary to analysis YAG and Ti-6Al-4V diffusion reaction with the same temperature and time.