Curing Characteristic of Blended Resins Prepared by Mixing Epoxy Resin with Phenol-liquefied Cryptomeria japonica and Properties of Their Cured Resins
碩士 === 國立中興大學 === 森林學系所 === 97 === In this study, Cryptomeria japonica (Japanese cedar) was liquefied in phenol with H2SO4 and HCl as a catalyst. The epoxy resin was synthesized from epichlorohydrin and bisphenol A with the molar ratio of 5/1. Blending resins were prepared by mixing the liquefied Ja...
Main Authors: | Chen-Ling Kang, 康甄玲 |
---|---|
Other Authors: | 李文昭 |
Format: | Others |
Language: | zh-TW |
Published: |
2009
|
Online Access: | http://ndltd.ncl.edu.tw/handle/53416719396287381904 |
Similar Items
-
Properties of Novolac/Epoxy Alloy Resins Prepared from Liquefied Cryptomeria Japonica Wood
by: Chien-Fang Chu, et al.
Published: (2014) -
The Properties Analysis forCryptomeria Japonica Treated Wood With Addition Curing Phenolic Resin
by: Yu-Chun Huang, et al.
Published: (2005) -
Cold-Setting Resorcinol Resin Adhesives Prepared from Phenol/Resorcinol Liquefied Cryptomeria japonica
by: Kuo-Chun Chang, et al.
Published: (2008) -
Preparation of Phenol-liquefied Cryptomeria japonica-based Alcohol Soluble Phenolic Resins and Their Application in The Manufacture of Particleboards and Woodceramics
by: Chia-Ju Chou, et al.
Published: (2009) -
Application of Liquefied Wood for Preparing Epoxidized Novolac-type Phenol-Formaldehyde Resins and the Properties of Cured Resins
by: Han-Min Hsieh, et al.
Published: (2011)