The study of the Inorganic Flame Retardant with Bisphenol A series of Epoxy Resin

• Main Authors: CHIA-JUNG HSU, 許家榮
• Other Authors: none
• Format: Others
• Language: zh-TW
• Published: 2007
• Online Access: http://ndltd.ncl.edu.tw/handle/kbevp9

碩士 === 國立臺灣科技大學 === 高分子系 === 95 === This study was research the component of inorganic flame retardant and application to plastic materials, we have discussion the influence of flame retarded properties with various ratio of additive on matrix, according to thermal analysis, and we also discussed the mechanism affect of degradation behavior of materials with flame retardant, and to used the UL94 burning test, limited oxygen index (CNS 13590) to determined the efficacy of flame retarded properties and charcoals rate. The result shows that could protract time to be aflame of epoxy resins as due to the inorganic flame retardant was addition, but its need appropriate ratio to bring the flame retarded effect, this effect was not satisfactory when only addition Antimony trioxide, but it have synergistic with addition aluminum hydroxide at the same time, it’s possible that it will to form a protect film to isolated the air of environment, the TGA thermal properties was show that aeration to decrease the oxygen contents of air at high temperature, furthermore, the composites of aluminum hydroxide with Antimony trioxide, aluminum hydroxide with magnesium hydroxide were obtained the fine flame retarded properties, respectively.