The analysis of fatigue properties in the advancing & retreating side of FSW

• Main Authors: Wu-chi Li, 李武奇
• Other Authors: Chung-Hung Lin
• Format: Others
• Language: zh-TW
• Published: 2007
• Online Access: http://ndltd.ncl.edu.tw/handle/40507649207411280008

碩士 === 國立成功大學 === 系統及船舶機電工程學系碩博士班 === 95 === ABSTRACT This text make with FSW Cheng carry on research , observe it make Cheng to aluminium alloy influence , A5083-O of material, expect that from observes it in the result of its static test , the behavior characteristic that tired cracks produced develop after rational explanation FSW is welded , use FSW is it sew idea of joint to have , mend the welding and mending working of the tired crack actually. And make Cheng Zhong's temperature field to distribute with FEM simulation , and verify the result welded in FEM simulation by surveying temperature, expect to be able to apply to the work on the spot. The ones that study and carry on are divided into three directions: (1)Carry on the static experiment , including the hardness amount examines, remains examining in conformity with strength examining and temperature amount. And then weld the side of about a line of edge and grow up and test from the vertical tired crack which weld a direction, analyse the static influence on the tired result of the test of result, understand because FSW causes and welds the influence of different nature of both sides . (2)Use FEM simulation distribution of temperature field when making Cheng , understand in advance that welds the temperature profile that the parameter causes. (3)Use FSW to be applied to mend in because the tired crack produced , and the tired behavior of observing it before and after mending.