Improving Hydrogen Storage Characteristics of Mg-based materials by slightly adding of Pd catalyst
碩士 === 國立清華大學 === 材料科學工程學系 === 93 === In this paper, we investigated the hydrogen storage properties of Mg + FeTi alloy with slightly Pd catalyst adding. The powder was prepared by high-energy ball milling under the argon atmosphere. In the different compositions of Pd ranged from 0.1% ~ 5%, the res...
| Main Authors: | , |
|---|---|
| Other Authors: | |
| Format: | Others |
| Language: | zh-TW |
| Published: |
2005
|
| Online Access: | http://ndltd.ncl.edu.tw/handle/89325590798711468292 |
| id |
ndltd-TW-093NTHU5159051 |
|---|---|
| record_format |
oai_dc |
| spelling |
ndltd-TW-093NTHU51590512016-06-06T04:11:21Z http://ndltd.ncl.edu.tw/handle/89325590798711468292 Improving Hydrogen Storage Characteristics of Mg-based materials by slightly adding of Pd catalyst 微量鈀添加改善鎂基儲氫材料之性質研究 Hsu Wei-chun 徐偉竣 碩士 國立清華大學 材料科學工程學系 93 In this paper, we investigated the hydrogen storage properties of Mg + FeTi alloy with slightly Pd catalyst adding. The powder was prepared by high-energy ball milling under the argon atmosphere. In the different compositions of Pd ranged from 0.1% ~ 5%, the results showed the improving hydrogen absorption kinetics and higher storage capacities at 50℃ and 150℃ respectively. We also compared the different milling time of Mg alloys, better hydrogen storage characteristics were achieved with increasing milling times, which results from finer particle sizes and more structure defects. Chen Jiann-Ruey 陳建瑞 2005 學位論文 ; thesis 65 zh-TW |
| collection |
NDLTD |
| language |
zh-TW |
| format |
Others
|
| sources |
NDLTD |
| description |
碩士 === 國立清華大學 === 材料科學工程學系 === 93 === In this paper, we investigated the hydrogen storage properties of Mg + FeTi alloy with slightly Pd catalyst adding. The powder was prepared by high-energy ball milling under the argon atmosphere. In the different compositions of Pd ranged from 0.1% ~ 5%, the results showed the improving hydrogen absorption kinetics and higher storage capacities at 50℃ and 150℃ respectively. We also compared the different milling time of Mg alloys, better hydrogen storage characteristics were achieved with increasing milling times, which results from finer particle sizes and more structure defects.
|
| author2 |
Chen Jiann-Ruey |
| author_facet |
Chen Jiann-Ruey Hsu Wei-chun 徐偉竣 |
| author |
Hsu Wei-chun 徐偉竣 |
| spellingShingle |
Hsu Wei-chun 徐偉竣 Improving Hydrogen Storage Characteristics of Mg-based materials by slightly adding of Pd catalyst |
| author_sort |
Hsu Wei-chun |
| title |
Improving Hydrogen Storage Characteristics of Mg-based materials by slightly adding of Pd catalyst |
| title_short |
Improving Hydrogen Storage Characteristics of Mg-based materials by slightly adding of Pd catalyst |
| title_full |
Improving Hydrogen Storage Characteristics of Mg-based materials by slightly adding of Pd catalyst |
| title_fullStr |
Improving Hydrogen Storage Characteristics of Mg-based materials by slightly adding of Pd catalyst |
| title_full_unstemmed |
Improving Hydrogen Storage Characteristics of Mg-based materials by slightly adding of Pd catalyst |
| title_sort |
improving hydrogen storage characteristics of mg-based materials by slightly adding of pd catalyst |
| publishDate |
2005 |
| url |
http://ndltd.ncl.edu.tw/handle/89325590798711468292 |
| work_keys_str_mv |
AT hsuweichun improvinghydrogenstoragecharacteristicsofmgbasedmaterialsbyslightlyaddingofpdcatalyst AT xúwěijùn improvinghydrogenstoragecharacteristicsofmgbasedmaterialsbyslightlyaddingofpdcatalyst AT hsuweichun wēiliàngbǎtiānjiāgǎishànměijīchǔqīngcáiliàozhīxìngzhìyánjiū AT xúwěijùn wēiliàngbǎtiānjiāgǎishànměijīchǔqīngcáiliàozhīxìngzhìyánjiū |
| _version_ |
1718296195378446336 |