Studies on the Mechanical Properties and Corrosion Wear Behavior of SiC<p>/A390 Al-matrix Composites
碩士 === 國立臺灣師範大學 === 工業教育研究所 === 87 === The primary purpose of this research was to investigate the effects of SiC particles (SiC<p>) size (46μm、80μm ) and the amount of reinforcements (5wt%、10wt%), solid solution treatment (480℃,3 hours), articificial aging (150℃, 1、3、10 hours) and the environ...