Manufacture and Improved Properties of Dyed Bamboo- Plastic Combinations-Treated with Styrene-

• Main Authors: Ping-Fei Lin, 林娉妃
• Other Authors: Kun-Fu Liao
• Format: Others
• Language: zh-TW
• Published: 1994
• Online Access: http://ndltd.ncl.edu.tw/handle/55839579198427789230

碩士 === 國立中興大學 === 森林學系 === 82 === The main results are summarized as follows： 1.It is di fferent between monomer loading and polymer loadi ng at bamboo speies， and the polymer loading decreasing with the increasing specific gravity at oven dry. 2.Among the three species，Green bamboo showed the highest m onomer loading. The effect of the polymerization of Green bamboo appeared the better. 3.Dyes would inhibite the reaction of polymerization of monom er .Swelling action of organic solvents could assist the formatio n of grafting in the cell walls，also shorten the distance betwee n monomer and cell wall. 4.Ma bamboo the improved effect of water-excluding efficiency and the improved effect of antishrink efficiency was the highest among the three species. 5.The hardness and cleavability are the highest， whereas sta tic bending strength was the opposite. 6.Ma bamboo appeared to have the highest improved effect in the abrassive resistance. 7.The order of light resistance for untreated bamboo was Thor ny bamboo，Greenen bamboo then Mabamboo，while the dyed BPC was G reen bamboo，Thorny bamboo then Ma bamboo. 8.The BPC showing higher strength reservation，and the better weathering resistance.The weight reservation of BPC was higher th an that of untreated bamboo.