| Summary: | A key part of the development of new polymeric materials focuses on the use of flame-retardant additives, which help to reduce the inherent flammability of polymers and the production of smoke and toxic gases.
The aim of this thesis was the preparation, characterization and application of new polymeric flame-retardant additives, which can lead to intumescent systems when mixed with ¨commodity¨ polymers. The synthesis of this kind of additives was carried out by chemical modification of different polymeric structures (alcohols, polyketones, polyaziridines) with phosphorous moieties, previously described as promoting flame retardance structures, and/or nitrogen containing moieties.
The efficacy of some of these additives was tested by blending with polypropylene, one of the most commonly used thermoplastic. Flame retardancy behaviour of the blends, as well their compatibility and mechanical properties were studied, in order to observe how the flame retardant additives may affect the substrate properties. === Una parte fundamental del desarrollo de nuevos materiales poliméricos se centra en la utilización de agentes retardantes a la llama, los cuales contribuyen a reducir la inherente combustibilidad de los polímeros y la producción de humos y de gases tóxicos.
El objetivo del presente trabajo ha sido la preparación, characterización y aplicación de nuevos aditivos retardantes a la llama de tipo polimérico que pueden dar lugar al mezclarse con polímeros termoplásticos de gran consumo a sistemas de tipo intumescente.
La síntesis de estos additivos se ha llevado a cabo por modificación química de diferentes estructuras polimericas (alcoholes, policetonas, poliaziridinas) con compuestos fosforados, descritos previamente como promotores de retardancia a la llama y/o compuestos con nitrogeno.
La eficacidad de algunos de estos additivos ha sido estudiada por mezclarse con polipropileno, uno de los más utilizados termoplasticos.
|
|---|