Fatigue Life Assessment of 30CrNiMo8HH Steel Under Variable Amplitude Loading

Fatigue Life Assessment of 30CrNiMo8HH Steel Under Variable Amplitude Loading

Show other versions (1)

The actual service loading histories of most engineering components are characterized by variable amplitudes and are sometimes rather complicated. The goal of this study was to estimate the fatigue life of nickel-chromium-molybdenum 30CrNiMo8HH steel alloy under axial and pure torsion variable ampli...

Full description

Bibliographic Details
Main Author:	Ibrahim, Elfaitori
Language:	en
Published:	2013
Subjects:	Fatigue life Variable amplitude loading Damage accumulation Load sequence Mean stress Cycle counting Mechanical Engineering
Online Access:	http://hdl.handle.net/10012/7216

Similar Items

Fatigue Life Assessment of 30CrNiMo8HH Steel Under Variable Amplitude Loading
by: Ibrahim, Elfaitori
Published: (2013)

On the assessment of multiaxial fatigue damage under variable amplitude loading
by: V. Anes, et al.
Published: (2016-06-01)

On the assessment of multiaxial fatigue damage under variable amplitude loading
by: V. Anes, et al.
Published: (2016-07-01)

Random accumulated damage evaluation under multiaxial fatigue loading conditions
by: V. Anes, et al.
Published: (2015-07-01)

Investigation of Changes in Fatigue Damage Caused by Mean Load under Block Loading Conditions
by: Roland Pawliczek, et al.
Published: (2021-05-01)

Bending Fretting Fatigue Characteristics of 18CrNiMo7-6 Alloy Steel
by: SHEN Yan-tuan, et al.
Published: (2017-07-01)

Problems of Equivalent Load Amplitude in Fatigue Life Calculations
by: Ligaj Bogdan, et al.
Published: (2016-01-01)

Fatigue Damage Accumulation Modeling of Metals Alloys under High Amplitude Loading at Elevated Temperatures
by: Jarosław Szusta, et al.
Published: (2018-12-01)

Fatigue Characteristic of Designed T-Type Specimen under Two-Step Repeating Variable Amplitude Load with Low-Amplitude Load below the Fatigue Limit
by: Jin Gan, et al.
Published: (2021-01-01)

Critical plane approach to multiaxial variable amplitude fatigue loading
by: Yingyu Wang, et al.
Published: (2015-07-01)

A Modified Model for Nonlinear Fatigue Damage Accumulation of Turbine Disc Considering the Load Interaction Effect
by: Tudi Huang, et al.
Published: (2019-08-01)

A multiaxial incremental fatigue damage formulation using nested damage surfaces
by: Marco Antonio Meggiolaro, et al.
Published: (2016-06-01)

A multiaxial incremental fatigue damage formulation using nested damage surfaces
by: Marco Antonio Meggiolaro, et al.
Published: (2016-07-01)

Critical plane approach to multiaxial variable amplitude fatigue loading
by: Yingyu Wang, et al.
Published: (2015-06-01)

Mean Stress Effect on the Axial Fatigue Strength of DIN 34CrNiMo6 Quenched and Tempered Steel
by: Luis Pallarés-Santasmartas, et al.
Published: (2018-03-01)

Damages and resource of locomotive wheels used under the north operating conditions
by: A. V. Grigorev, et al.
Published: (2014-01-01)

Principal Features of Fatigue and Residual Strength of Composite Materials Subjected to Constant Amplitude (CA) Loading
by: Alberto D’Amore, et al.
Published: (2019-08-01)

Multiaxial Fatigue and Deformation Including Non-proportional Hardening and Variable Amplitude Loading Effects
by: Shamsaei, Nima
Published: (2010)

Estimation of fatigue lifetime for selected metallic materials under multiaxial variable amplitude loading
by: Yingyu Wang, et al.
Published: (2016-06-01)

Estimation of fatigue lifetime for selected metallic materials under multiaxial variable amplitude loading
by: Yingyu Wang, et al.
Published: (2016-07-01)

Cumulative Damage and Life Prediction Models for High-Cycle Fatigue of Metals: A Review
by: Kris Hectors, et al.
Published: (2021-01-01)

Comparative Study of Phenomenological Residual Strength Models for Composite Materials Subjected to Fatigue: Predictions at Constant Amplitude (CA) Loading
by: Alberto D’Amore, et al.
Published: (2019-10-01)

Effect of nonlinear slamming loads on the fatigue damage of a ship with large flare
by: Xu Zhiting, et al.
Published: (2019-12-01)

Continuous Time Fatigue Modelling for Non-proportional Loading
by: Gundmi Satish, Sajjan
Published: (2019)

Optical Sensing of the Fatigue Damage State of CFRP under Realistic Aeronautical Load Sequences
by: Pablo Zuluaga-Ramírez, et al.
Published: (2015-03-01)

Fatigue crack growth of composite patch repaired Al-alloy plates under variable amplitude loading
by: Fatima Zohra Seriari, et al.
Published: (2017-12-01)

Fatigue crack growth of composite patch repaired Al-alloy plates under variable amplitude loading
by: Fatima Zohra Seriari, et al.
Published: (2018-01-01)

Enhanced strain-based fatigue methodology for high strength aluminum alloys
by: Arcari, Attilio
Published: (2014)

Comparative study of multiaxial fatigue methods applied to welded joints in marine structures
by: P.S. van Lieshout, et al.
Published: (2016-06-01)

Comparative study of multiaxial fatigue methods applied to welded joints in marine structures
by: P.S. van Lieshout, et al.
Published: (2016-07-01)

On the applicability of Miner’s rule for multiaxial fatigue life calculations under non-proportional load histories
by: Marco Antonio Meggiolaro, et al.
Published: (2017-06-01)

On the applicability of Miner’s rule for multiaxial fatigue life calculations under non-proportional load histories
by: Marco Antonio Meggiolaro, et al.
Published: (2017-07-01)

Measuring variable amplitude loading with fibre optic
by: Assanah, N., et al.
Published: (2018)

Fatigue Reliability Analysis of a Compressor Disk Based on Probability Cumulative Damage Criterion
by: Jungang Ren, et al.
Published: (2020-05-01)

The mean stress influence on lifetime under high-cycle fatigue combined loading
by: Balda M., et al.
Published: (2013-06-01)

SIMULATION OF CRACK GROWTH LIFE IN THE SKIN ELEMENTS OF AVIATION CONSTRUCTIONS UNDER VARIABLE-AMPLITUDE LOADING[
by: V. V. Nikonov, et al.
Published: (2016-11-01)

Study on SLM Forming Process, Residual Stress and Thermal Fatigue of 24CrNiMo Alloy Steel
by: Yongsheng Zhao, et al.
Published: (2021-08-01)

Study on Inclusions Distribution and Cyclic Fatigue Performance of Gear Steel 18CrNiMo7-6 Forging
by: Min Wang, et al.
Published: (2020-01-01)

Functional Behavior of Pseudoelastic NiTi Alloy Under Variable Amplitude Loading
by: Iasnii Volodymyr, et al.
Published: (2020-09-01)

Estudo do efeito de pausas introduzidas em testes de fadiga de amplitude variável.
by: Clayton Mamedes Angelo
Published: (2016)