Synthesis of the Vanadium Oxide Compounds and Investigation by X-Ray Photoelectron Spectroscopy Method

• Main Author: Pašiškevičius, Audrius
• Other Authors: Bondarenka, Vladimiras
• Format: Doctoral Thesis
• Language: English
• Published: Lithuanian Academic Libraries Network (LABT) 2011
• Subjects: Physics; XPS; Sol-gel; Vanadium; Bronze; Rentgeno fotoelektronų spektroskopija; Zolis-gelis; Vanadis; Bronza
• Online Access: http://vddb.laba.lt/fedora/get/LT-eLABa-0001:E.02~2011~D_20110219_122819-95620/DS.005.1.01.ETD

The thin films of oxide xerogels and bronzes and molecular oxide xerogels and bronzes of vanadium compounds were synthesized by sol-gel technology method. The chemical composition of mentioned compounds was investigated using XPS method in order to determine the valence of metal ions. It is shown that it is possible to produce the thin films of vanadium oxide bronzes using simple methods. The possibility to use vanadium-ammonium oxide hydrated compounds as materials for producing the ammonium sensors is shown in the dissertation. === Šiame darbe panaudojant zolis-gelis technologiją, susintetinti vanadžio junginių oksidinių kserogelių ir bronzos bei molekulinių oksidinių kserogelių ir bronzų plonieji sluoksniai. Visų minėtų medžiagų cheminė sudėtis ištirta Rentgeno fotoelektronų spektroskopijos metodu, siekiant nustatyti metalų jonų valentines būsenas. Panaudojant zolis-gelis technologiją, galima gana paprastais metodais, nenaudojant sudėtingos technologinės įrangos, gaminti vanadžio oksidinių bronzų plonuosius sluoksnius. Vanadžio amonio hidratuoti oksidiniai junginiai gali būti naudojami kaip medžiagos amoniako dujų jutikliams gaminti.