| Summary: | Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgico === FundaÃÃo de Amparo à Pesquisa do Estado do Cearà === This work reports the preparation and characterization of collagen-sulfated polysaccharide films and applications in coating of cardiovascular prostheses. The films were prepared by adding the sulfated polysaccharide solution on soluble collagen (0, 5, 10, 20 and 25 %). The blends of collagen-sulfated polysaccharide were casted in acrylic molds, and dried at low temperature. The physico-chemical properties of collagen-sulfated polysaccharide films, were studied using infrared spectroscopy that showed absorptions typical of collagen and sulphated polysaccharide; the thermal analysis (DSC) showed that the structural integrity of collagen was unmodified during the extraction process and the polysaccharide present in the samples did not decrease the thermal stability of the collagen, which was higher for the concentrations of 20 %. In the thermal analysis (DTG), the addition of the polysaccharide caused a small decrease of the stability of thermal degradation and when was adding 5 % of the sulfated polysaccharide to the collagen, a reduction in its stability occurs, however, in the concentrations of 10, 20 and 25 %, the stability of thermal degradation of the film increased. In the impedance spectroscopy, the results are associated possibly, to the interactions between the macromolecules. The blood compatibility was analyzed by platelet adhesion and the results showed that the films possess hemocompatibility and antitrombogenic properties. === Este trabalho aborda sobre o preparo e a caracterizaÃÃo de filmes de colÃgeno-polissacarÃdeo sulfatado e sua aplicaÃÃo para revestimento de prÃteses vasculares. Os filmes foram obtidos a partir da mistura de soluÃÃo de colÃgeno e polissacarÃdeo sulfatado, nas concentraÃÃes 0, 5, 10, 20 e 25 % do polissacarÃdeo. As soluÃÃes de colÃgeno-polissacarÃdeo sulfatado foram formatadas em moldes de acrÃlico em condiÃÃes de baixa umidade e temperatura. A caracterizaÃÃo fÃsico-quÃmica dos filmes de colÃgeno-polissacarÃdeo sulfatado foi estudada por espectrometria no infravermelho que mostraram bandas tÃpicas do colÃgeno e bandas tÃpicas do polissacarÃdeo sulfatado; a anÃlise tÃrmica por DSC mostra que a integridade estrutural do colÃgeno foi preservada no processo de extraÃÃo e que a adiÃÃo do polissacarÃdeo nas amostras nÃo diminuiu a estabilidade tÃrmica do colÃgeno tendo sido maior na concentraÃÃo de 20 %. Na anÃlise tÃrmica por DTG, a adiÃÃo do polissacarÃdeo causa um pequeno decrÃscimo da estabilidade de degradaÃÃo tÃrmica e ao adicionarmos 5 % do polissacarÃdeo sulfatado ao colÃgeno, ocorre uma reduÃÃo em sua estabilidade, porÃm, a partir daÃ, nas concentraÃÃes 10, 20 e 25 %, a estabilidade de degradaÃÃo tÃrmica do filme vai aumentando. Na espectroscopia de impedÃncia, os resultados estÃo associados, possivelmente, a interaÃÃes entre as macromolÃculas. A compatibilidade sangÃÃnea foi analisada por adesÃo de plaquetas e os resultados mostraram que os filmes possuem hemocompatibilidade e propriedades antitrombogÃnicas.
|
|---|