Efeito das varia??es do pH na resist?ncia de uni?o e na nanoinfiltra??o de sistemas adesivos ? dentina

• Main Author: Manfroi, Fernanda Borguetti
• Other Authors: Spohr, Ana Maria
• Format: Others
• Language: Portuguese
• Published: Pontif?cia Universidade Cat?lica do Rio Grande do Sul 2018
• Subjects: Ciclos de pH; Dentina; Resist?ncia de Uni?o; Sistemas Adesivos; CIENCIAS DA SAUDE::ODONTOLOGIA
• Online Access: http://tede2.pucrs.br/tede2/handle/tede/7879

Submitted by PPG Odontologia ([e-mail]) on 2018-03-09T13:09:24Z No. of bitstreams: 1 FERNANDA_BORGUETTI_MANFROI_TES.pdf: 2715505 bytes, checksum: 81352bd5d757e75e046659bb79849f86 (MD5) === Approved for entry into archive by Tatiana Lopes ([e-mail]) on 2018-03-12T12:58:50Z (GMT) No. of bitstreams: 1 FERNANDA_BORGUETTI_MANFROI_TES.pdf: 2715505 bytes, checksum: 81352bd5d757e75e046659bb79849f86 (MD5) === Made available in DSpace on 2018-03-12T13:06:37Z (GMT). No. of bitstreams: 1 FERNANDA_BORGUETTI_MANFROI_TES.pdf: 2715505 bytes, checksum: 81352bd5d757e75e046659bb79849f86 (MD5) Previous issue date: 2018-01-16 === Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES === (Artigo 1 - Efeito dos ciclos de pH na resist?ncia de uni?o de diferentes sistemas adesivos ? dentina) Purpose: To verify the influence of the pH cycles on the microtensile bond strength (?TBS) to dentin of three adhesive systems compared to the immediate ?TBS and after storage in artificial saliva for 6 months. Materials and methods: The occlusal surface of 32 sound third molar teeth was removed to obtain a flat dentin surface. The teeth were randomly divided into four groups (n=8/group): G1 - Single Bond Universal in the total-etch mode; G2 ? Single Bond Universal in the self-etch mode; G3 ? Scotchbond Multi Purpose (totaletch mode control); G4 ? Clearfil SE Bond (self-etch mode control). A block of composite with 6 mm height was built on the adhesive area. After 24 h of storage in distilled water at 37?C, the tooth/resin sets were cut parallel to the long axis of the tooth, in the x and y directions, with a section of approximately 0.8 mm2 . Fifty-two specimens were obtained for each group, of which 26 were submitted to pH cycles and the other 26 were stored in artificial saliva for 6 months. Subsequently, the specimens were submitted to a ?TBS test in a universal testing machine at a crosshead speed of 0.5 mm/min. For the immediate evaluation (24 h), results previously obtained were used for this study. Results: According to the two-way ANOVA test, the interaction between the factors (p=0.0001) was significant. There was no significant difference in the immediate ?TBS between the adhesive systems. After 4 cycles of pH and 6 months of storage in artificial saliva, there was a significant decrease in ?TBS for all adhesive systems. The failures were predominantly mixed. Conclusion: The pH cycles and the storage in artificial saliva for 6 months were detrimental to the stability of the bonding interface. (Artigo 2 - Efeito dos ciclos de pH na nanoinfiltra??o de diferentes sistemas adesivos ? dentina) Purpose: To verify the influence of the pH cycles on the nanoleakage in the dentin-adhesive interface of three adhesive systems compared to the immediate nanoleakage and after storage in artificial saliva for 6 months. Materials and methods: The occlusal surface of 24 sound third molar teeth was removed to obtain a flat dentin surface. The teeth were randomly divided into four groups (n=6/group): G1 ? Single Bond Universal in the total-etch mode; G2 ? Single Bond Universal in the self-etch mode; G3 ? Scotchbond Multi Purpose (total-etch mode control); G4 ? Clearfil SE Bond (self-etch mode control). A block of composite with 6 mm height was built on the adhesive area. After 24 h of storage in distilled water at 37?C, the tooth/resin sets were cut parallel to the long axis of the tooth to obtain slices with a thickness of approximately 1.0 mm. Three slices of the central region of each tooth were obtained. One slice was submitted to pH cycles, and one slice was stored in artificial saliva for 6 months. The nanoleakage methodology was applied. Images of the dentin-adhesive interfaces were obtained by scanning electron microscopy (2000x), and the images were analyzed in the ImageJ program to evaluate the percentage of nanoleakage area (%N). Results: According to the two-way ANOVA test, the interaction between the factors (adhesive system x storage) (p=0.0001) was significant. There was no significant difference in the %N between the adhesive systems at 24 h. After the pH cycles, the adhesive systems applied in the self-etch mode obtained lower %N, differing significantly from total-etch adhesives. After 6 months in artificial saliva, there was lower %N compared to pH cycles, and the lowest %N occurred in self-etch adhesives. Conclusion: The pH cycles caused higher nanoleakage than storage in artificial saliva for 6 months. The self-etch adhesive systems had lower nanoleakage after pH cycles and storage in artificial saliva for 6 months in relation to total-etch adhesive systems. === (Artigo 1 - Efeito dos ciclos de pH na resist?ncia de uni?o de diferentes sistemas adesivos ? dentina) Objetivo: Verificar a influ?ncia dos ciclos de pH nos valores de resist?ncia de uni?o ? microtra??o (R?T) ? dentina de tr?s sistemas adesivos em compara??o com a R?T imediata e ap?s armazenamento em saliva artificial pelo per?odo de 6 meses. Materiais e m?todos: A superf?cie oclusal de 32 dentes terceiros molares h?gidos foi removida para obter superf?cie plana em dentina, sendo divididos aleatoriamente em quatro grupos (n=8/grupo): G1 ? Single Bond Universal na vers?o total-etch; G2 ? Single Bond Universal na vers?o self-etch; G3 ? Scotchbond Multi Purpose (controle da vers?o total-etch); G4 ? Clearfil SE Bond (controle da vers?o self-etch). Sobre o sistema adesivo foi confeccionado um bloco de 6 mm de altura em resina composta. Ap?s 24 h de armazenagem em ?gua destilada a 37?C, os conjuntos dente/resina foram cortados paralelamente no longo eixo do dente, nos sentidos x e y, com sec??o de aproximadamente 0,8 mm2 . Cinquenta e dois corpos de prova foram obtidos, em m?dia, para cada grupo, sendo 26 submetidos aos ciclos de pH, e os outros 26 ao armazenamento em saliva artificial por 6 meses. Na sequ?ncia, os corpos de prova foram submetidos ao teste de microtra??o em m?quina de ensaio universal EMIC DL-2000, com uma velocidade de 0,5 mm/min. Os tipos de falha foram observados em microscopia eletr?nica de varredura. Para a avalia??o imediata (24 h) foram utilizados resultados obtidos previamente a este estudo. Resultados: De acordo com o teste ANOVA de duas vias a intera??o entre os fatores (p=0,0001) foi significativa. N?o houve diferen?a estat?stica na R?T imediata entre os sistemas adesivos. Ap?s os 4 ciclos de pH e 6 meses de armazenamento em saliva artificial houve redu??o significativa das m?dias de R?T para todos os sistemas adesivos. As falhas foram predominantemente mistas. Conclus?o: Os ciclos de pH e o armazenamento em saliva artificial durante 6 meses prejudicaram a estabilidade da interface de uni?o. (Artigo 2 - Efeito dos ciclos de pH na nanoinfiltra??o de diferentes sistemas adesivos ? dentina) Objetivo: Verificar a influ?ncia dos ciclos de pH na nanoinfiltra??o da interface dentina-adesivo de tr?s sistemas adesivos em compara??o com a nanoinfiltra??o imediata e ap?s armazenamento em saliva artificial por 6 meses. Materiais e m?todos: A superf?cie oclusal de 24 dentes terceiros molares h?gidos foi removida para obter superf?cie plana em dentina, sendo divididos aleatoriamente em quatro grupos (n=6/grupo): G1 ?Single Bond Universal na vers?o total-etch; G2 ? Single Bond Universal na vers?o self-etch; G3 ? Scotchbond Multi Purpose (controle da vers?o total-etch); G4 ? Clearfil SE Bond (controle da vers?o self-etch). Sobre o sistema adesivo foi confeccionado um bloco de 6 mm de altura em resina composta. Ap?s 24 h de armazenagem em ?gua destilada a 37?C, os conjuntos dente/resina foram cortados paralelamente no longo eixo do dente, resultando em fatias, com espessura de aproximadamente 1,0 mm. Tr?s fatias da regi?o central de cada dente foram obtidas, sendo uma fatia submetida aos ciclos de pH, e uma fatia armazenada em saliva artificial por 6 meses. Na sequ?ncia foi aplicada a metodologia de nanoinfiltra??o. Imagens das interfaces dentina-adesivo foram obtidas por meio de microscopia eletr?nica de varredura (2000x), sendo as imagens analisadas no programa ImageJ para avaliar a porcentagem de ?rea de nanoinfiltra??o (%N). Resultados: De acordo com o teste ANOVA de duas vias, a intera??o dos fatores (sistema adesivo x armazenamento) foi significativa (p=0,0001). N?o houve diferen?a estat?stica na %N entre os sistemas adesivos na avalia??o em 24 h. Ap?s os ciclos de pH os sistemas adesivos aplicados de maneira self-etch obtiveram menor %N, diferindo estatisticamente dos adesivos total-etch. Ap?s 6 meses em saliva artificial, houve menor %N comparado aos ciclos de pH, e as menores %N ocorreram nos adesivos self-etch. Conclus?o: Os ciclos de pH causaram maior nanoinfiltra??o do que o armazenamento em saliva artificial por 6 meses. Os sistemas adesivos aplicados de maneira selfetch tiveram menor nanoinfiltra??o ap?s os ciclos de pH e armazenamento em saliva artificial por 6 meses em rela??o aos sistemas adesivos total-etch.