| Summary: | Made available in DSpace on 2016-08-19T12:56:39Z (GMT). No. of bitstreams: 1
dissertacao Fernanda.pdf: 1549685 bytes, checksum: d2b56a7ad60c89efdf1404d7658ae95a (MD5)
Previous issue date: 2012-07-06 === Coordenação de Aperfeiçoamento de Pessoal de Nível Superior === In this work, nanocatalysts of Pt/C, PtRe/C PtIr C and PtW/C supported on carbon were prepared by the alcohol reduction process and characterized by transmission electron microscopy (TEM), X-ray Diffraction (XRD), Energy Dispersive X-ray (EDX) and X-ray photoelectron spectroscopy (XPS). The electrochemical behavior of nano catalysts in the presence of ethanol and glycerol were evaluated by cyclic voltammetry (CV) and chronoamperometry. The results indicated that the nanoparticles PtRe/C showed better catalytic performance in the range of interest potential for direct alcohol fuel cells, up to 0.6 V. It can be suggested that this behavior is due to the presence of Re that intensified the catalyst performance aiding the formation of more reactive sites to improve the oxidation process. === Neste trabalho, nanocatalisadores de Pt/C, PtRe/C, PtIr/C e PtW/C suportados em carbono foram preparados pelo método de redução por álcool e caracterizados usando as técnicas de Microscopia eletrônica de transmissão (MET), Difração de raios-X (DRX), Energia Dispersiva de raios-X (EDX) e Espectroscopia fotoeletrônica de raios X (XPS). O comportamento eletroquímico dos nanocatalisadores frente às reações de oxidação de etanol e glicerol foi avaliado por voltametria cíclica (VC) e cronoamperometria. Os resultados mostraram que as nanopartículas de PtRe/C apresentaram melhor desempenho catalítico na faixa de potenciais de interesse para células à combustível. Pode-se sugerir que este comportamento se deve a presença do Re que intensificou o desempenho do catalisador auxiliando a formação de sítios mais reativos para melhorar o processo de oxidação.
|
|---|