Influência da pigmentação, técnica de união e envelhecimento acelerado sobre a resistência de união entre resina acrílica e silicone facial

• Main Author: Haddad, Marcela Filié [UNESP]
• Other Authors: Universidade Estadual Paulista (UNESP)
• Format: Others
• Language: Portuguese
• Published: Universidade Estadual Paulista (UNESP) 2014
• Subjects: Resinas acrilicas; Elastômeros de silicone; Nanopartículas; Protese maxilo-facial; Envelhecimento; Acrylic resins
• Online Access: http://hdl.handle.net/11449/108706

Made available in DSpace on 2014-08-13T14:50:52Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-06-28Bitstream added on 2014-08-13T18:00:07Z : No. of bitstreams: 1 000764939.pdf: 4285251 bytes, checksum: 9da5ef190038848837a8d33e81f903b8 (MD5) === Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) === Próteses maxilofaciais retidas por implantes necessitam de uma infraestrutura acrílica, na qual ficam contidos os sistemas de retenção; contudo, a união resina acrílica-silicone facial não é estável. Assim, este estudo teve como objetivo avaliar a influência da pigmentação com nanopartículas, técnica de união e envelhecimento acelerado sobre a resistência de união entre resina acrílica e silicone facial. Para tal, foram confeccionadas 960 amostras que consistiam em uma barra de resina acrílica de ativação química aderida ao silicone facial Silastic MDX 4-4210 incolor ou pigmentado com nanopartículas (tinta a óleo e/ou opacificador a base de sulfato de bário). A adesão entre os dois materiais foi feita pela simples deposição do silicone sobre a resina acrílica (N); por retenções mecânicas, representadas por ranhuras (R); aplicação do primer de uso médico (DC 1205 Prime - DC); primer para material reembasador (Sofreliner Primer MS- SF) ou adesivo de uso médico (Silatic Medical Adhesive Type A - A) isolados ou associados. Desta maneira, as amostras foram divididas em 4 grupos (n=240), de acordo com a nanopartícula adicionada ou não, sendo Grupo 1: Incolor; Grupo 2: Tinta a óleo; Grupo 3: Opacificador; e Grupo 4: Tinta a óleo e opacificador. Estes grupos foram divididos em 12 subgrupos (n=20), de acordo com o meio utilizado para unir a resina acrílica ao silicone, sendo: Subgrupo I: N; Subgrupo II: A; Subgrupo III: DC; Subgrupo IV: DC+A; Subgrupo V: SF; Subgrupo VI: SF+A; Subgrupo VII: R; Subgrupo VIII: R+A; Subgrupo IX: R+DC; Subgrupo X: R+DC+A; Subgrupo XI: R+SF; Subgrupo XII: R+SF+A. Metade das amostras de... === Maxillofacial prosthesis retained by implants use an acrylic framework to fit the attachment systems. However, the bond between acrylic resin and facial silicone is instable. Therefore, this study investigated the influence of nanoparticles pigments, adhesive system and accelerated aging on the bond strength between the acrylic resin and facial silicone. A total of 960 specimens made of selfpolymerized acrylic resin bar adhered to Silastic MDX 4-4210 facial silicone either colorless or pigmented with nanoparticles (oil tint and/or barium sulfate opacifier) were fabricated. The union between the two materials was performed in different ways: no treatment on the acrylic bar (N), mechanical retentions represented by scratches (R), application of prime for medical use (DC 1205 Prime - DC), primer for soft liner material (Sofreliner Primer MS - SF), and adhesive for medical use (Silastic Medical Adhesive Type A - A) alone or in combinations. The specimens were divided into 4 groups (n=240) according to the nanoparticle presence: Group 1: colorless; Group 2: oil tint; Group 3: opacifier; and Group 4: oil tint and opacifier. These groups were divided into 12 subgroups (n=20) according to the surface treatment used to bond the facial silicone to the acrylic resin: Subgroup I: N; Subgroup II: A; Subgroup III: DC; Subgroup IV: DC+A; Subgroup V: SF; Subgroup VI: SF+A; Subgroup VII: R; Subgroup VIII: R+A; Subgroup IX: R+DC; Subgroup X: R+DC+A; Subgroup XI: R+SF; Subgroup XII: R+SF+A. Half of the specimens of each subgroup (n=10) were subjected to bond strength test at the baseline period in a universal testing machine at a crosshead speed of 10 mm/min until failure. The other specimens were exposed to the accelerated... === FAPESP: 10/02937-1