| Summary: | Made available in DSpace on 2014-06-11T19:31:26Z (GMT). No. of bitstreams: 0
Previous issue date: 2008-03-26Bitstream added on 2014-06-13T19:41:14Z : No. of bitstreams: 1
alvim_hh_dr_arafo.pdf: 694477 bytes, checksum: 944910958f33686fa33839611d4acf41 (MD5) === Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) === O objetivo deste estudo foi avaliar as características de diferentes fotoinciadores com potencial para serem utilizados em resinas compostas. Foram utilizadas as resinas compostas: Filtek Z250 A3 (FZA3); Filtek Z-250 Incisal (FZI); Pyramid Enamel A1 (PEA1); Piramyd Enamel Translucent (PET); Filtek Supreme A3E (FSA3) e Filtek Supreme GT (FSGT). Foram pesados 500mg de cada resina e dissolvidos em 1,0 ml de metanol. As amostras foram centrifugadas para acelerar a sedimentação das partículas inorgânicas. Foram pipetados 0,8 ml da solução sobrenadante e analisados por cromatografia gasosa acoplado ao espectrômetro de massa (GC-MS). Os resultados foram comparados a soluções de canforoquinona pura, utilizadas como padrão. O teste de T Student, (p=0,05), comparou os resultados entre as cores de cada marca comercial. Observou-se menor quantidade de canforoquinona na cor incisal da resina Filtek Z-250 (FZI) quando comparada à cor A3 (FZA3). Por outro lado, a resina Filtek Supreme apresentou quantidade de canforoquinona estatisticamente superior na cor Incisal. Na resina Pyramid Enamel foi encontrada canforoquinona apenas na cor A1, sendo que o fotoiniciador utilizado na cor Translucent não foi identificado. Baseado nos dados obtidos pode-se concluir que uma mesma marca comercial de resina composta pode apresentar diferenças na quantidade e no tipo de fotoiniciador utilizado. Em seguida investigamos a reação de polimerização de quatro compósitos experimentais por fotocalorimetria, utilizando diferentes fotoiniciadores. Esta técnica permite estimar o grau de conversão (GC) e parâmetros da cinética da reação como a aceleração da reação em tempo real. Foi elaborada uma resina composta experimental, a base de Bis-GMA (14,5% m/m), UDMA (6,5% m/m) e partículas de carga silanizadas (79% m/m). Este compósito foi dividido em quatro grupos, que receberam os seguintes fotoiniciadores:... === To identify and quantify the camphorquinone (CQ) used in different brands of composite resins as a function of the shade analyzed. Filtek Z250 A3 (FZA3), Filtek Z- 250 Incisal (FZI), Pyramid Enamel A1(PEA1), Pyramid Enamel Translucent (PET), Filtek Supreme A3E (FSA3) and Filtek Supreme GT (FSGT) were used. Five hundred milligrams of each resin were weighed and then dissolved in 1.0 ml of methanol. The samples were centrifuged to accelerate the sedimentation of the inorganic particles. 0.8 ml of the supernatant solution was collected with a pipette and assessed under gas chromatography coupled to the mass spectrometer (GC–MS). The results were compared to pure CQsolutions, used as a standard. Student’s t-test, (p = 0.05) significant at the level of 5%, compared the results of each brand shade. A smaller amount of camphorquinone was found in Filtek Z-250 (FZI) resin incisal shade when compared to (FZA3) A3 shade. On the other hand, Filtek Supreme resin featured a statistically larger camphorquinone amount in the incisal shade. In Pyramid Enamel resin camphorquinone was found only in shade A1, while the photoinitiator used in the Translucent shade was not identified. Then we investigate the reaction of polymerization of four experimental composites by fotocalorimetria, using different photoinitiators. This technique allows estimating the degree of conversion (GC) and kinetic parameters of the reaction as the acceleration of the reaction in real time. It was drawn up a composite resin experimental, the basis of Bis-GMA (14.5% m / m), UDMA (6.5% m / m) and particulate load silanizadas (79% m / m). This composite was divided into four groups, which received the following fotoiniciadores: camphorquinone (CQ), 1-phenyl-1 ,2-propanodione (PPD), MAPO (Lucirin TPO) and BAPO (Irgacure 819). The reaction of polymerization of these four experimental composite was analyzed...(Complete abstract, click electronic access below)
|
|---|
