Propriedades ópticas da alumina anódica porosa e o efeito do guia de onda

• Main Author: Carossi, Lory Cantelli
• Other Authors: Strixino, Francisco Trivinho
• Language: Portuguese
• Published: Universidade Federal de São Carlos 2017
• Subjects: Óxido de alumínio; Alumina anódica porosa; Interferências de Fabry-Pérot; Espectroscopia de retroespalhamento de Rutherford; Filmes finos - Propriedades ópticas; Aluminum oxide; Thin films - Optical properties; Nanoporous Anodic Alumina; Fabry-Pérot interference; Composition analysis; CIENCIAS EXATAS E DA TERRA::QUIMICA::FISICO-QUIMICA
• Online Access: https://repositorio.ufscar.br/handle/ufscar/9003

Submitted by Milena Rubi ([e-mail]) on 2017-08-16T17:19:17Z No. of bitstreams: 1 CAROSSI_Lory_2017.pdf: 61131706 bytes, checksum: 687def06b5a758fcb457d49f53a494b1 (MD5) === Approved for entry into archive by Milena Rubi ([e-mail]) on 2017-08-16T17:19:27Z (GMT) No. of bitstreams: 1 CAROSSI_Lory_2017.pdf: 61131706 bytes, checksum: 687def06b5a758fcb457d49f53a494b1 (MD5) === Approved for entry into archive by Milena Rubi ([e-mail]) on 2017-08-16T17:19:33Z (GMT) No. of bitstreams: 1 CAROSSI_Lory_2017.pdf: 61131706 bytes, checksum: 687def06b5a758fcb457d49f53a494b1 (MD5) === Made available in DSpace on 2017-08-16T17:19:39Z (GMT). No. of bitstreams: 1 CAROSSI_Lory_2017.pdf: 61131706 bytes, checksum: 687def06b5a758fcb457d49f53a494b1 (MD5) Previous issue date: 2015-02-11 === Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) === Nanoporous anodic alumina films (NAA) may present different behavior to reflectance and photoluminescence techniques, with Fabry-Pérot interferences and waveguide properties. This phenomenon makes possible the use of NAA as transducer signal in optical sensors. In this work, we investigated how the pre-treatment, the number of steps of anodizing, the anodizing electrolyte mode and temperature affect electrochemical characteristics, morphological and optical mainly NAA. As a result, it was noticeable that the realization of electropolishing is necessary for both the NAA with good regularity as to make it possible to obtain a spectrum with the Fabry-Pérot interference. If the fabrication of NAA is done in two steps, it is possible to obtain reflectance spectra and luminescence fringed with better amplitudes, areas and heights. Regarding the anodizing mode, both the NAA anodized in galvanostatic how potentiostatic showed similar morphologies and spectra with fringes, but the interferences were better defined when the galvanostatic mode was performed. Regarding the temperature, it was noticeable that the change of this parameter leads influences the porous oxide thickness. The spectrum of the luminescence and reflectance increasing the electrolyte temperature caused an increase in interference. However, the range and resolution of interference decreased with increasing temperature. The oxide thicknesses were estimated by energy variation (?E), graph slope between order and 1/? and fast Fourier transform (FFT) techniques. The ratio of film thickness and pore diameter (L/dp) was performed to validate the NAA films with better waveguides property. Moreover, the surface composition analysis of NAA films anodized in phosphoric acid, oxalic acid and mixtures thereof by backscattering spectroscopy Rutherford (RBS) was performed. From simulations it was possible to note that the amount of carbon in the porous oxide structure is practically zero, which may indicate that the origin of the luminescence is related to the presence of more centers F. === Filmes de alumina anódica porosa (AAP) podem apresentar, espectros de reflectância e luminescência com interferências de Fabry-Pérot e propriedades de guias de onda. Esse fenômeno possibilita que a AAP possa ser utilizada como plataforma em sensores ópticos. Neste trabalho, foi investigado como o pré-tratamento, o número de etapas de anodização, o modo de anodização e a temperatura do eletrólito afetam características eletroquímicas, morfológicas e principalmente ópticas da AAP. Como resultado, foi possível notar que a realização do eletropolimento é necessário para obter tanto a AAP com boa regularidade como para que seja possível obter um espectro com as interferências Fabry-Pérot. Se a fabricação da AAP for feita em duas etapas, é possível obter espectros de reflectância e luminescência com franjas com melhores amplitudes, áreas e alturas. Com relação ao modo de anodização, tanto as AAPs anodizadas em modo galvanostático como potenciostático apresentaram morfologias semelhantes e espectros com franjas, mas as interferências foram melhor definidas quando o modo galvanostático foi realizado. Com relação à temperatura, foi possível notar que a mudança desse parâmetro ocasiona influencia na espessura do óxido poroso. Quanto aos espectros de luminescência e reflectância, o aumento da temperatura do eletrólito ocasionou um aumento no número de interferências. Entretanto, a amplitude e a resolução das interferências diminuíram com o aumento da temperatura. A espessura do filme poroso foi estimada pelas técnicas de variação de energia (?E), coeficiente angular do gráfico entre ordem da interferência e 1/? e através da transformada rápida de Fourier (FFT). E foi utilizada a razão entre a espessura do filme e diâmetro do poro (Esp/Dp) para averiguar os filmes de AAP com guias de onda que pudessem ser utilizadas como substratos para sensores ópticos. Além disso, foi realizada a análise de composição superficial dos filmes de AAP anodizados em ácido fosfórico, oxálico e mistura destes ácidos pela técnica de espectroscopia de retroespalhamento de Rutherford (RBS). A partir das simulações realizadas foi possível notar que a quantidade que carbono na estrutura do oxido poroso é praticamente nula, o que pode indicar que a origem da luminescência está relacionada à presença dos centros F.