| Summary: | Made available in DSpace on 2016-06-02T20:16:42Z (GMT). No. of bitstreams: 1
1816.pdf: 2942981 bytes, checksum: c07401a4b38696ecd78cf0c96ac0c526 (MD5)
Previous issue date: 2008-03-13 === Financiadora de Estudos e Projetos === Electric and magnetic properties of nanoscopic clusters of iron immersed in Zinc
Selenide were studied in this work. The system presents superparamagnetic behavior with a
weak thermally activate ferromagnetic interaction. Small tunnel magnetoresistence was
observed in room temperature (approximately 1% with fields of 30 kOe) and its behavior
was observed as a function of temperature and bias. This work demonstrate that a despite of
excellent macroscopic and microscopic properties of Fe/ZnSe/Fe epitaxial heterostructures
the experimental observation shows small values of tunnel magnetoristance in room
temperature. This results shows that the application of this materials in spintronics devices
is limited. === As propriedades elétricas e magnéticas de aglomerados nanoscópicos de Fe imersos
em matriz de ZnSe foram investigadas. Foi observado que este sistema apresenta um
comportamento superparamagnético com pequena interação ferromagnética termicamente
ativada. Também foi observada pequena taxa de magnetorresistência túnel em temperatura
ambiente (da ordem de 1% para campos de 30 kOe) e observamos o comportamento desta
com a temperatura e tensão. O estudo demonstra que, apesar das estruturas epitaxiais
Fe/ZnSe/Fe possuírem propriedades microscópicas e macroscópicas necessárias à aplicação
em junções túnel magnéticas, a observação experimental apresenta baixas taxas de TMR
em temperatura ambiente, o que desencoraja os materiais para aplicações em dispositivos
spintrônicos.
|
|---|