| Summary: | Submitted by Nathalya Silva (nathyjf033@gmail.com) on 2017-04-24T20:06:13Z
No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Tese_ObtencaoCaracterizacaoOuro.pdf: 4109766 bytes, checksum: 5c0eb5d0a3c676e4dca07445c5b51344 (MD5) === Approved for entry into archive by Edisangela Bastos (edisangela@ufpa.br) on 2017-04-26T13:54:59Z (GMT) No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Tese_ObtencaoCaracterizacaoOuro.pdf: 4109766 bytes, checksum: 5c0eb5d0a3c676e4dca07445c5b51344 (MD5) === Made available in DSpace on 2017-04-26T13:54:59Z (GMT). No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Tese_ObtencaoCaracterizacaoOuro.pdf: 4109766 bytes, checksum: 5c0eb5d0a3c676e4dca07445c5b51344 (MD5)
Previous issue date: 2014-06 === CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior === O ouro e suas diversas ligas tem maior aplicação como adorno em peças de joalheria, mas o ouro puro não apresenta dureza necessária para essa utilização. Por essa razão é geralmente endurecido com outros metais. Foram obtidas quatro (4) ligas de ouro, sendo (1) um intermetálico Au20%Al de cor violeta e três (3) de coloração usual na fabricação de joias (Au-25%Ag – verde claro, Au-12,5%Cu – vermelha Au-12,5%Ag-12,5%Cu – amarela). Propõe-se introduzir o uso do intermetálico e a melhoria na produção de ligas para setor joalheiro por meio da elaboração e caracterização das propriedades óticas, estruturais e mecânicas. Foram obtidas no Laboratório de Materiais da Faculdade de Engenharia Química da Universidade Federal do Pará (UFPA) e a liga Au-20%Al foi produzida nas oficinas de microprodutores do estado do Pará. As propriedades estruturais foram analisadas por meio de microscopia ótica (MO) e eletrônica de varredura (MEV). A partir das análises foi revelada estrutura celular dendrítica para as ligas Au-25%Ag e Au-12,5%Cu, estrutura dendrítica para a liga Au-12,5%Ag-12,5%Cu e estrutura celular para a liga Au-20%Al. As propriedades mecânicas foram obtidas através de ensaios de microdureza Vickers, verificando-se a maior dureza na liga Au-20%Al, intermetálico do tipo AX2. As propriedades óticas observadas por meio de ensaios de colorimetria, utilizando-se colorímetro, onde se evidenciaram espectros de luz visível dentro da faixa de cor violeta (Au-20%Al), amarelo esverdeada (Au-25%Ag), vermelho (Au-12,5%Cu), e amarelo (Au-12,5%Ag-12,5%Cu). === Gold has main application as adornment in jewelry pieces but in its pure state doesn’t have the hardness required for this use, being generally fused with other metals to form alloys. The aim of this research was to elaborate and characterize optical, structural and mechanical properties of gold alloys and introduce the use of intermetallic Au-20% Al, seeking to improve the production of jewelry industry. Four (4) gold alloys were prepared: one (1) intermetallic Au-20% Al violet colored and three (3) with usual coloration in jewelry manufacture (Au-25% Ag - light green, Au-12,5% Cu - red, Au-12,5% Ag-12,5% Cu - yellow). Au-20% Al alloy was produced in microproducers of the state of Pará workshops, while the others were fused in Materials Laboratory of Chemical Engineering School in Federal University of Pará (UFPA). The structural properties were analyzed by optical microscopy (OM) and scanning electron microscopy (SEM). The results revealed dendritic cell structure for Au-25% Ag and Au-12,5% Cu alloys, dendritic structure for Au-12,5% Ag-12,5% Cu alloy and cellular structure for Au-20% Al alloy. The mechanical properties were obtained through Vickers microhardness tests, evidencing the highest hardness for Au-20% Al alloy, intermetallic of AX2 type. The optical properties evaluated by colorimetric tests showed visible light spectrum in the range from violet color (Au-20% Al), greenish yellow (Au-25% Ag), red (Au-12,5% Cu) and yellow (Au-12,5% Ag-12,5% Cu).
|
|---|