Estudo da hidrogenação para pulverização de ligas à base de terras raras com Nb para eletrodos de hidreto metálico

• Main Author: FERREIRA, ELINER A.
• Other Authors: Rubens Nunes de Faria Júnior
• Format: Others
• Published: 2013
• Subjects: primary-secondary hybrid batteries; electric batteries; chemical reactions; hydrogenation; comminution; crushing; nickel base alloys; rare earth alloys; hydrides; electrodes; electrical testing; materials handling equipment; scanning electron microscopy; x-ray diffraction
• Online Access: http://repositorio.ipen.br:8080/xmlui/handle/123456789/26390

Submitted by Claudinei Pracidelli ([e-mail]) on 2016-06-22T13:51:24Z No. of bitstreams: 0 === Made available in DSpace on 2016-06-22T13:51:24Z (GMT). No. of bitstreams: 0 === Neste trabalho foram estudadas as series de ligas La0,7Mg0,3Al0,3Mn0,4Co(0,5-x)NbxNi3,8 (x =0 a 0,5) e La0,7Mg0,3Al0,3Mn0,4Nb(0,5-x)Ni(3,8-x) (x =0,3; 0,5 e 1,3), como eletrodo negativo de baterias de Níquel Hidreto Metálico. A pulverização das ligas foi realizada com duas pressões de H2 (2 bar e 9 bar). A capacidade de descarga das baterias de níquel hidreto metálico foi analisada pelo equipamento de testes elétricos Arbin BT-4. As ligas, no estado bruto de fusão, foram analisadas por microscopia eletrônica de varredura (MEV), espectroscopia de energia dispersiva (EDS) e difração de raios-X. Com o aumento da concentração de nióbio nas ligas nota-se a diminuição da estabilidade cíclica das baterias e da capacidade máxima de descarga. A capacidade de descarga máxima obtida foi para a liga La0,7Mg0,3Al0,3Mn0,4Co0,5Ni3,8 (45,36 mAh) e a bateria que apresentou a melhor performance foi a liga La0,7Mg0,3Al0,3Mn0,4Co0,4Nb0,1Ni3,8 (44,94 mAh). === Tese (Doutorado em Tecnologia Nuclear) === IPEN/T === Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP