Propriedades mecânicas e avaliação microscópica de fios ortodônticos de niti revestidos por polímeros

• Main Author: Ferreira, Gaudyer Castro Di
• Other Authors: Lenza, Marcos Augusto
• Format: Others
• Language: Portuguese
• Published: Universidade Federal de Goiás 2016
• Subjects: Fios ortodônticos; Propriedades superficiais; Microscopia eletrônica de varredura; Orthodontic wires; Surface properties; Microscopy; CIENCIAS DA SAUDE::ODONTOLOGIA
• Online Access: http://repositorio.bc.ufg.br/tede/handle/tede/5263

Submitted by Luciana Ferreira ([e-mail]) on 2016-02-23T11:24:55Z No. of bitstreams: 2 Dissertação - Gaudyer Castro di Ferreira - 2015.pdf: 12501436 bytes, checksum: 06af9912db4067aacec6a4dec872f91a (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) === Approved for entry into archive by Luciana Ferreira ([e-mail]) on 2016-02-23T11:27:08Z (GMT) No. of bitstreams: 2 Dissertação - Gaudyer Castro di Ferreira - 2015.pdf: 12501436 bytes, checksum: 06af9912db4067aacec6a4dec872f91a (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) === Made available in DSpace on 2016-02-23T11:27:08Z (GMT). No. of bitstreams: 2 Dissertação - Gaudyer Castro di Ferreira - 2015.pdf: 12501436 bytes, checksum: 06af9912db4067aacec6a4dec872f91a (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Previous issue date: 2015-03-24 === The objective of the study was to analyze the mechanical properties and analyze the surface of the wires coated polymers. Methods: We used the pre-contoured wires study with dimension of 0.014 "Nickel- Titanium (NiTi) brands: Tecident orthodontic equipment Ltda (São Carlos, São Paulo Brazil), TP Orthodontics (Indiana, USA), Trianeiro ( Rio Claro, São Paulo Brazil) and NiTi wire Morelli (Sorocaba, Sao Paulo Brazil) as a control group. The yarns were randomly divided into 11 groups (n = 6) .There were carried deflection test. The yarns were immersed in artificial saliva for a period of 30 to 60 days to corrode. After the wire corrosion were also submitted for the analysis of Scanning Electron Microscopy (SEM). Results: We used the ANOVA analysis of variance, which were statistically significant differences between the tested wire and the controle.Foram group observed imperfections on the surfaces of all the wire and the wire TP Orthodontics showed the greatest changes. Conclusions: The polymeric coating appears to be responsible for the mechanical surface change and the NiTi wires. === O objetivo do estudo foi analisar as propriedades mecânicas e analisar a superfície, dos fios revestidos por polímeros. Materiais e métodos: Foram utilizados no estudo fios pré-contornados com dimensão de 0.014” de Niquel-Titânio (NiTi) das marcas: Tecident Equipamento Ortodonticos Ltda(São Carlos,São Paulo Brasil), TP Orthodontics (Indiana, EUA) , Trianeiro (Rio Claro, São Paulo Brasil) e fio NiTi Morelli ( Sorocaba, São Paulo Brasil) como grupo controle. Os fios foram divididos aleatoriamente em 11 grupos (n=6).Foram realizado o teste de deflexão. Os fios foram imersos em saliva artificial por um período de 30 e 60 dias,para sofrer corrosão. Após a corrosão os fio também foram submetidos para a análise de Microscopia Eletrônica de Varredura (MEV). Resultados:Foi utilizado o teste de variância ANOVA, onde foram observadas diferenças estatisticamente significantes entre os fios testados e os do grupo controle.Foram observadas imperfeições nas superfícies de todos os fio sendo que o fio da TP Orthodontics apresentou as maiores alterações. Conclusões: O revestimento polimérico parece ser o responsável pelas alterações mecânicas e da superfície dos fios de NiTi.