Citotoxicidade de cimentos de ionômero de vidro com adição de nanopartículas de prata

• Main Author: Siqueira, Patrícia Correia de
• Other Authors: Lopes, Lawrence Gonzaga
• Format: Others
• Language: Portuguese
• Published: Universidade Federal de Goiás 2015
• Subjects: Cimentos de ionômeros de vidro; Citotoxicidade; Técnicas de cultura de células; Nanotecnologia; Nanopartículas metálicas; Glass ionomer cements; Cytotoxicity; Cell culture techniques; Nanotechnology; Metal nanoparticles; CIENCIAS DA SAUDE::ODONTOLOGIA
• Online Access: http://repositorio.bc.ufg.br/tede/handle/tede/4429

Submitted by Luciana Ferreira ([e-mail]) on 2015-04-20T12:55:10Z No. of bitstreams: 2 Dissertação - Patrícia Correia de Siqueira - 2014.pdf: 1536081 bytes, checksum: 16162d6f2185a664f1f75daf7492fb8c (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) === Approved for entry into archive by Luciana Ferreira ([e-mail]) on 2015-04-20T12:58:41Z (GMT) No. of bitstreams: 2 Dissertação - Patrícia Correia de Siqueira - 2014.pdf: 1536081 bytes, checksum: 16162d6f2185a664f1f75daf7492fb8c (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) === Made available in DSpace on 2015-04-20T12:58:41Z (GMT). No. of bitstreams: 2 Dissertação - Patrícia Correia de Siqueira - 2014.pdf: 1536081 bytes, checksum: 16162d6f2185a664f1f75daf7492fb8c (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Previous issue date: 2014-02-03 === Fundação de Amparo à Pesquisa do Estado de Goiás - FAPEG === The aim of this study was to evaluate and compare the cytotoxicity of two glass ionomer cements (GIC), a conventional (GC Gold Label 1 – GC Corporation) and a resin modified (Vitrebond – 3M ESPE), both indicated for lining, with and without addition of silver nanoparticles (NAg). The NAg were incorporated at the materials in two different concentrations by weight: 0.1% and 0.2%. Specimens with standardized dimensions (4 x 2 mm) were prepared, and for preparing liquid extracts of the cements, the specimens were immersed in 400 μL of culture medium and incubated at 37°C and 5% CO2 for 48 hours. The extracts obtained were incubated in contact with cells for 48 hours. As negative and positive controls were used respectively culture medium and solution of NAg at 0.78% by weight. To evaluate cellular viability, MTT and Trypan Blue assays were used. Data were subjected to statistical analysis with ANOVA and Tukey (α=0.05). Significant decrease in cell viability was observed in all groups of Vitrebond (p˂0.001) compared to negative control. There were no statistically significant differences between the groups of this cement with and without NAg (p˃0.05). For GC Gold Label 1, no statistically significant differences were observed in cell viability between any of the groups compared with the negative control (p>0.05). There was also no difference between the groups with and without NAg (p>0.05). The positive control showed significant reduction in cell viability (p˂0.001). It is concluded that the NAg did not influence on cytotoxicity of GICs evaluated. === O objetivo do presente trabalho foi avaliar e comparar a citotoxicidade de dois cimentos de ionômero de vidro (CIV) indicados para forramento, sendo um convencional (GC Gold Label 1 – GC Corporation) e um modificado por resina (Vitrebond – 3M ESPE), com e sem adição de nanopartículas de prata (NAg). As NAg foram incorporadas aos materiais durante sua manipulação em duas concentrações em massa: 0,1% e 0,2%. Espécimes com dimensões padronizadas (4 x 2 mm), com e sem NAg, foram confeccionados, e para o preparo de extratos líquidos dos cimentos, os espécimes foram imersos em 400 μL de meio de cultura e incubados em estufa a 37ºC e 5% de CO2 por 48 horas. Os extratos obtidos foram incubados em contato com as células por 48 horas em estufa. Como controles negativo e positivo foram usados, respectivamente, meio de cultura e solução de NAg a 0,78% em massa. Dois testes para realizar a avaliação da viabilidade celular foram utilizados: o ensaio colorimétrico do MTT e o ensaio de Azul de Tripano. Os dados obtidos foram tabulados e submetidos à análise estatística com ANOVA e Tukey (α=0,05). Foi observada redução significativa na viabilidade celular em todos os grupos do Vitrebond (p˂0,001), em comparação ao controle negativo. Não foram observadas diferenças estaticamente significantes entre os grupos desse cimento com NAg e o grupo sem NAg (p˃0,05). Para o GC Gold Label 1, não foram observadas diferenças estaticamente significantes da viabilidade celular entre os grupos experimentais em comparação ao controle negativo (p>0,05). Também não houve diferença significante entre os grupos com NAg e sem NAg (p>0,05). No controle positivo observou-se redução significante da viabilidade celular (p˂0,001). Pela metodologia empregada, concluiu-se que as NAg não influenciaram na citotoxicidade dos CIVs avaliados.