| Summary: | === In this work a new self-assembly technique is presented, allowing the fast formation of carbon black thin films. It consists in the controlled addition of a stable carbon material's dispersion over the water surface, disturbed by a vortex. The vortex, although not essential for the film formation, was found to drastically improve film homogeneity. A physical chemical study concerning how several parameters could be used to tune film properties was also conducted. The selfassembled
films, which can be picked up in any hydrophilic substrate, showed a good electrical conductivity and a high optical transparency. As an application example, films about 200 nm thick were employed as supercapacitor electrodes. === O propósito deste trabalho foi estudar uma nova técnica que possibilita a formação de filmes finos de carbon black em poucos minutos. O procedimento consiste na adição controlada de uma dispersão estável do material de carbono sobre a superfície da água, perturbada por um vórtice. Foi observado que a presença do vórtice possibilita a obtenção de filmes com maior homogeneidade. Foi realizada, ainda, uma investigação físico-química dos diversos fatores que infuenciam as propriedades dos filmes. Os filmes obtidos podem ser coletados em virtualmente qualquer substrato hidrofílico e apresentam boa condutividade elétrica e alta transparência. Como exemplo de aplicação, filmes com cerca de 200 nm de espessura foram utilizados como eletrodos de supercapacitor.
|
|---|