EVALUATION OF THE RESISTANCE TO SULPHIDE STRESS CORROSION CRACKING AND HYDROGEN EMBRITTLEMENT OF API 5L -X80 GIRTH WELDS

EVALUATION OF THE RESISTANCE TO SULPHIDE STRESS CORROSION CRACKING AND HYDROGEN EMBRITTLEMENT OF API 5L -X80 GIRTH WELDS

PONTIFÍCIA UNIVERSIDADE CATÓLICA DO RIO DE JANEIRO === COORDENAÇÃO DE APERFEIÇOAMENTO DO PESSOAL DE ENSINO SUPERIOR === CONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO === FUNDAÇÃO DE APOIO À PESQUISA DO ESTADO DO RIO DE JANEIRO === PROGRAMA DE SUPORTE À PÓS-GRADUAÇÃO DE INSTS. DE ENSI...

Full description

Bibliographic Details
Main Author:	ADRIANA FORERO BALLESTEROS
Other Authors:	IVANI DE SOUZA BOTT
Language:	Portuguese
Published:	PONTIFÍCIA UNIVERSIDADE CATÓLICA DO RIO DE JANEIRO 2009
Online Access:	http://www.maxwell.vrac.puc-rio.br/Busca_etds.php?strSecao=resultado&nrSeq=32706@1 http://www.maxwell.vrac.puc-rio.br/Busca_etds.php?strSecao=resultado&nrSeq=32706@2

Similar Items

[en] EVALUATION OF THE RESISTANCE TO SULPHIDE STRESS CORROSION CRACKING AND HYDROGEN EMBRITTLEMENT OF API 5L -X80 GIRTH WELDS
by: ADRIANA FORERO BALLESTEROS
Published: (2018)

Evaluation of the diffusivity and susceptibility to hydrogen embrittlement of API 5L X80 steel welded joints
by: B Araújo, et al.
Published: (2016-09-01)

Stress corrosion cracking and hydrogen embrittlement of stainless steels
by: Bilogan, K. W.
Published: (1980)

EVALUATION OF THE MICROSTRUCTURAL AND MECHANICAL PROPERTIES OF THE GIRTH WELDING OF AN API 5L X80 STEEL TUBE BY SEMI-AUTOMATIC WELDING PROCESSES WITH GAS SHIELDING
by: RICHARD ZACARIAS SANZ DURAND
Published: (2007)

Microstructure and properties of the interlayer heat-affected zone in X80 pipeline girth welds
by: Fang Bai, et al.
Published: (2020-02-01)

[en] EVALUATION OF THE MICROSTRUCTURAL AND MECHANICAL PROPERTIES OF THE GIRTH WELDING OF AN API 5L X80 STEEL TUBE BY SEMI-AUTOMATIC WELDING PROCESSES WITH GAS SHIELDING
by: RICHARD ZACARIAS SANZ DURAND
Published: (2007)

The tensile properties and toughness of microstructures relevant to the HAZ of X80 linepipe steel girth welds
by: Gaudet, Michael J.
Published: (2015)

Corrosion fatigue crack growth and hydrogen embrittlement in high strength aluminium alloy 7150
by: Gingell, Andrew Donald Brian
Published: (1994)

Residual stress evaluation in API 5L X65 girth welded pipes joined by friction welding and gas tungsten arc welding
by: Carlos Alexandre Pereira de Moraes, et al.
Published: (2019-01-01)

Slow-strain-rate-hydrogen embrittlement and stress-corrosion cracking in ti-al binary alloys
by: Mauney, David Alexander
Published: (2006)

Stress corrosion cracking and hydrogen embrittlement of thick section high strength low alloy steel.
by: Needham, William Donald
Published: (2012)

Stress corrosion cracking and hydrogen embrittlement of thick section high strength low alloy steel
by: Needham, William Donald
Published: (2007)

Towards an explanation of liquid metal embrittlement cracking in resistance spot welding of dissimilar steels
by: Zhanxiang Ling, et al.
Published: (2020-10-01)

Low temperature and hydrogen embrittlement properties of API 5L X65 steel and weldment
by: Y. J. Lin, et al.
Published: (1999)

A strong and ductile medium-entropy alloy resists hydrogen embrittlement and corrosion
by: Hong Luo, et al.
Published: (2020-06-01)

Surface residual stress effects on stress corrosion cracking/hydrogen embrittlement behavior of AISI 4340 steel
by: Hays, Richard A.
Published: (2017)

Hydrogen Sulphide Stress Corrosion Cracking of 2.25Cr-Mo Steel Weldments
by: Lin, W.L., et al.
Published: (1997)

Hydrogen Embrittlement Sensitivity of Laser Welded T-200 Maraging Steel
by: Wu, Chien-Peng, et al.
Published: (1998)

Study on the Fracture Toughness of Friction Stir Welded API X80
by: Tribe, Allan M.
Published: (2012)

On the Stress Corrosion Cracking and Hydrogen Embrittlement Behavior of Austenitic Stainless Steels in Boiling Saturated Magnesium Chloride Solutions
by: Osama M. Alyousif, et al.
Published: (2012-01-01)

A calculation method for limit load of the gas pipelines with girth weld surface cracks
by: Xu Wang, et al.
Published: (2019-10-01)

Nanocrystalline Steels’ Resistance to Hydrogen Embrittlement
by: Skołek E., et al.
Published: (2015-04-01)

Effects of different cooling rates on the microstructure, crystallographic features, and hydrogen induced cracking of API X80 pipeline steel
by: Mario F.G. Ramirez, et al.
Published: (2021-09-01)

Study on the effect of welding joint design on the hydrogen embrittlement susceptibility of weldments
by: Chen, Yean-Tsorng, et al.
Published: (1998)

Author Correction: A strong and ductile medium-entropy alloy resists hydrogen embrittlement and corrosion
by: Hong Luo, et al.
Published: (2020-07-01)

Hydrogen Embrittlement and Sub-Critical Crack Growth in Hydride Forming Metals
by: Varias, A.G.
Published: (2005-06-01)

Residual life assessment of welded joints in the girth weld root
by: Shron Leonid, et al.
Published: (2020-01-01)

Residual stresses in girth butt welded pipes
by: Scaramangas, A.
Published: (1984)

The structure and properties of mechanized pipeline girth welds
by: Boothby, Peter James
Published: (1989)

Fracture toughness of mechanised pipeline girth welds
by: Tinston, S. F.
Published: (1988)

Hydrogen Embrittlement of Cold-worked 304L Stainless Steel and its Welds
by: Chien-Lin Lai, et al.
Published: (2011)

Effect of Hydrogen Embrittlement and Strain Rate Sensitivity in the Laser Welds of Maraging Steel
by: Huang, W. B., et al.
Published: (1996)

The relationship of weld metal hardness residual stress and susceptible to stress corrosion cracking in hydrogen sulphide environment in A516 Grade 70 carbon steel shielded metal arc welded joint
by: De Beer, Deon Johan
Published: (2019)

Numerical evaluation of multipass welding temperature field in API 5L X80 steel welded joints
by: J Nóbrega, et al.
Published: (2016-10-01)

Fracture modeling of resistance spot welded ultra-high-strength steel considering the effect of liquid metal embrittlement crack
by: Yunwu Ma, et al.
Published: (2021-11-01)

Hydrogen embrittlement of 4340 steel as a result of corrosion of porous cadmium electroplate.
by: Rinker, John George
Published: (2006)

The Prevention of Hydrogen Embrittlement and Corrosion Problems for Metallic Materials Used in Petroleum Refineries.
by: Chen Chun Lin, et al.
Published: (1993)

Fatigue Crack Growh of Welded API 5L X65 Linepipes
by: Yung Cheng Chen, et al.
Published: (1999)

Study on Temper Embrittlement and Hydrogen Embrittlement of a Hydrogenation Reactor by Small Punch Test
by: Kaishu Guan, et al.
Published: (2017-06-01)

Computer Modeling of Localised Heat Treatment of Girth Welds
by: V. Bychkov, et al.
Published: (2015-09-01)

Cannot write session to /tmp/vufind_sessions/sess_27bdac21hggdlu5rkbbgipr5lu