EXPERIMENTAL DETERMINATION OF FRACTURE TOUGHNESS OF MODE I (KIC) AND MODE II (KIIC) DO BAMBOO
PONTIFÍCIA UNIVERSIDADE CATÓLICA DO RIO DE JANEIRO === CONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO === FUNDAÇÃO DE APOIO À PESQUISA DO ESTADO DO RIO DE JANEIRO === Durante as ultimas três décadas, as pesquisas cientificas sobre bambu como material de engenharia concentraram-se na c...
Main Author: | |
---|---|
Other Authors: | |
Language: | Portuguese |
Published: |
PONTIFÍCIA UNIVERSIDADE CATÓLICA DO RIO DE JANEIRO
2009
|
Online Access: | http://www.maxwell.vrac.puc-rio.br/Busca_etds.php?strSecao=resultado&nrSeq=16005@1 http://www.maxwell.vrac.puc-rio.br/Busca_etds.php?strSecao=resultado&nrSeq=16005@2 |
id |
ndltd-IBICT-oai-MAXWELL.puc-rio.br-16005 |
---|---|
record_format |
oai_dc |
collection |
NDLTD |
language |
Portuguese |
sources |
NDLTD |
description |
PONTIFÍCIA UNIVERSIDADE CATÓLICA DO RIO DE JANEIRO === CONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO === FUNDAÇÃO DE APOIO À PESQUISA DO ESTADO DO RIO DE JANEIRO === Durante as ultimas três décadas, as pesquisas cientificas sobre bambu
como material de engenharia concentraram-se na caracterização física e
mecânica nos níveis macro, meso, micro e alguns trabalhos no nível nanoestructural.
As praticas de uso de bambu inteiro mostram ao longo do tempo
trincas na superfície que são provocadas por razão da variação da umidade, da
temperatura e entalhes gerados durante o processo de fabricação de peças
estruturais. A presença das trincas tem grande influenciam na resistência
desses elementos. Este aspecto do comportamento do bambu ainda é assunto
de estudo na fase inicial. O presente trabalho apresenta os resultados da
pesquisa teórico-experimental realizada para a determinação dos valores
característicos dos fatores de intensidade de tensões, K(C), e as taxas de
dissipação de energia, G(C), para os modos I e II, utilizando metodologias
experimentais aplicadas aos materiais compósitos. Foi estudada a espécie
Dendrocalamus Giganteus da parte basal do bambu do campus da PUC-Rio. A
dimensão do corpo-de-prova tinha seção transversal retangular de 10x10mm e
100 mm de comprimento do vão livre com entalhes induzidos. Os corpos-deprova
foram submetidos à flexão em quatro pontos para diferentes valores de
tamanho de entalhe. São apresentados os resultados de carga-deslocamento
na metade do comprimento e as deformações relativas nas faces externa,
interna e lateral dos corpos-de-prova. Os valores das taxas dissipação de
energia e fatores de intensidade de tensões foram calculados a partir da curva
de carga - deslocamento. === During the last three decades, the research on bamboo as engineering
material was carried on through the physical and mechanic characterizations in
the levels macro, meso, micro and some works in the nano-structural level. In
practice, the use of entire bamboo shows cracks on the surface throughout the
time, that are provoked by variation of the moisture, the temperature and
notches generated during the process of manufacture of structural parts. The
crack presence has influences on the resistance of these elements. This aspect
of the bamboo behaviour is still subject of study in the initial phase. This work
presents the results of a theoretical and experimental research for the
determination of the characteristic values of the intensity stress factors, K(C), and
the release energy, G(C), for modes I and II, using methodologies applied to the
composites materials. It was studied the basal part of the specie
Dendrocalamus Giganteus of the Pontifícia Universidade Católica do Rio de
Janeiro campus (PUC-Rio). The specimens had rectangular shape with
transversal section of 10x10mm and 100mm of length with notch; each one was
tested in four points bend for different values of notch size. The results
correspond to curves load-displacement in the half span; and strain in the
external, internal and lateral sides of the specimen. The values of release
energy and intensity stress factors have been calculated from the curve loaddisplacement. |
author2 |
KHOSROW GHAVAMI |
author_facet |
KHOSROW GHAVAMI CAMILO ANDRES RUSINQUE GUATIBONZA |
author |
CAMILO ANDRES RUSINQUE GUATIBONZA |
spellingShingle |
CAMILO ANDRES RUSINQUE GUATIBONZA EXPERIMENTAL DETERMINATION OF FRACTURE TOUGHNESS OF MODE I (KIC) AND MODE II (KIIC) DO BAMBOO |
author_sort |
CAMILO ANDRES RUSINQUE GUATIBONZA |
title |
EXPERIMENTAL DETERMINATION OF FRACTURE TOUGHNESS OF MODE I (KIC) AND MODE II (KIIC) DO BAMBOO |
title_short |
EXPERIMENTAL DETERMINATION OF FRACTURE TOUGHNESS OF MODE I (KIC) AND MODE II (KIIC) DO BAMBOO |
title_full |
EXPERIMENTAL DETERMINATION OF FRACTURE TOUGHNESS OF MODE I (KIC) AND MODE II (KIIC) DO BAMBOO |
title_fullStr |
EXPERIMENTAL DETERMINATION OF FRACTURE TOUGHNESS OF MODE I (KIC) AND MODE II (KIIC) DO BAMBOO |
title_full_unstemmed |
EXPERIMENTAL DETERMINATION OF FRACTURE TOUGHNESS OF MODE I (KIC) AND MODE II (KIIC) DO BAMBOO |
title_sort |
experimental determination of fracture toughness of mode i (kic) and mode ii (kiic) do bamboo |
publisher |
PONTIFÍCIA UNIVERSIDADE CATÓLICA DO RIO DE JANEIRO |
publishDate |
2009 |
url |
http://www.maxwell.vrac.puc-rio.br/Busca_etds.php?strSecao=resultado&nrSeq=16005@1 http://www.maxwell.vrac.puc-rio.br/Busca_etds.php?strSecao=resultado&nrSeq=16005@2 |
work_keys_str_mv |
AT camiloandresrusinqueguatibonza experimentaldeterminationoffracturetoughnessofmodeikicandmodeiikiicdobamboo AT camiloandresrusinqueguatibonza determinacaoexperimentaldatenacidadedobambudomodoikicemodoiikiic |
_version_ |
1718987741443653632 |
spelling |
ndltd-IBICT-oai-MAXWELL.puc-rio.br-160052019-03-01T15:39:02Z EXPERIMENTAL DETERMINATION OF FRACTURE TOUGHNESS OF MODE I (KIC) AND MODE II (KIIC) DO BAMBOO DETERMINAÇÃO EXPERIMENTAL DA TENACIDADE DO BAMBU DO MODO I (KIC) E MODO II (KIIC) CAMILO ANDRES RUSINQUE GUATIBONZA KHOSROW GHAVAMI PAULO BATISTA GONCALVES KHOSROW GHAVAMI NORMANDO PERAZZO BARBOSA CONRADO DE SOUZA RODRIGUES CONRADO DE SOUZA RODRIGUES PONTIFÍCIA UNIVERSIDADE CATÓLICA DO RIO DE JANEIRO CONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO FUNDAÇÃO DE APOIO À PESQUISA DO ESTADO DO RIO DE JANEIRO Durante as ultimas três décadas, as pesquisas cientificas sobre bambu como material de engenharia concentraram-se na caracterização física e mecânica nos níveis macro, meso, micro e alguns trabalhos no nível nanoestructural. As praticas de uso de bambu inteiro mostram ao longo do tempo trincas na superfície que são provocadas por razão da variação da umidade, da temperatura e entalhes gerados durante o processo de fabricação de peças estruturais. A presença das trincas tem grande influenciam na resistência desses elementos. Este aspecto do comportamento do bambu ainda é assunto de estudo na fase inicial. O presente trabalho apresenta os resultados da pesquisa teórico-experimental realizada para a determinação dos valores característicos dos fatores de intensidade de tensões, K(C), e as taxas de dissipação de energia, G(C), para os modos I e II, utilizando metodologias experimentais aplicadas aos materiais compósitos. Foi estudada a espécie Dendrocalamus Giganteus da parte basal do bambu do campus da PUC-Rio. A dimensão do corpo-de-prova tinha seção transversal retangular de 10x10mm e 100 mm de comprimento do vão livre com entalhes induzidos. Os corpos-deprova foram submetidos à flexão em quatro pontos para diferentes valores de tamanho de entalhe. São apresentados os resultados de carga-deslocamento na metade do comprimento e as deformações relativas nas faces externa, interna e lateral dos corpos-de-prova. Os valores das taxas dissipação de energia e fatores de intensidade de tensões foram calculados a partir da curva de carga - deslocamento. During the last three decades, the research on bamboo as engineering material was carried on through the physical and mechanic characterizations in the levels macro, meso, micro and some works in the nano-structural level. In practice, the use of entire bamboo shows cracks on the surface throughout the time, that are provoked by variation of the moisture, the temperature and notches generated during the process of manufacture of structural parts. The crack presence has influences on the resistance of these elements. This aspect of the bamboo behaviour is still subject of study in the initial phase. This work presents the results of a theoretical and experimental research for the determination of the characteristic values of the intensity stress factors, K(C), and the release energy, G(C), for modes I and II, using methodologies applied to the composites materials. It was studied the basal part of the specie Dendrocalamus Giganteus of the Pontifícia Universidade Católica do Rio de Janeiro campus (PUC-Rio). The specimens had rectangular shape with transversal section of 10x10mm and 100mm of length with notch; each one was tested in four points bend for different values of notch size. The results correspond to curves load-displacement in the half span; and strain in the external, internal and lateral sides of the specimen. The values of release energy and intensity stress factors have been calculated from the curve loaddisplacement. 2009-07-24 info:eu-repo/semantics/publishedVersion info:eu-repo/semantics/masterThesis http://www.maxwell.vrac.puc-rio.br/Busca_etds.php?strSecao=resultado&nrSeq=16005@1 http://www.maxwell.vrac.puc-rio.br/Busca_etds.php?strSecao=resultado&nrSeq=16005@2 por info:eu-repo/semantics/openAccess PONTIFÍCIA UNIVERSIDADE CATÓLICA DO RIO DE JANEIRO PPG EM ENGENHARIA CIVIL PUC-Rio BR reponame:Repositório Institucional da PUC_RIO instname:Pontifícia Universidade Católica do Rio de Janeiro instacron:PUC_RIO |