Lattice anomalies and magnetic states in Fe_5Si_3-Mn_5Si_3 alloys
<p>The lattice anomalies and magnetic states in the (Fe<sub>100-x</sub>Mn<sub>x</sub>)<sub>5</sub>Si<sub>3</sub> alloys have been investigated. Contrary to what was previously reported, results of x-ray diffraction show a second phase (α') p...
| Summary: | <p>The lattice anomalies and magnetic states in the (Fe<sub>100-x</sub>Mn<sub>x</sub>)<sub>5</sub>Si<sub>3</sub> alloys have been investigated. Contrary to what was previously reported, results of x-ray diffraction show a second phase (α') present in Fe-rich alloys and therefore strictly speaking a complete solid solution does not exist. Mössbauer spectra, measured as a function of composition and temperature, indicate the presence of two inequivalent sites, namely 6(g) site (designated as site I) and 4(d) (site II). A two-site model (TSM) has been introduced to interpret the experimental findings. The compositional variation of lattice parameters a and c, determined from the x-ray analysis, exhibits anomalies at x = 22.5 and x = 50, respectively. The former can be attributed to the effect of a ferromagnetic transition; while the latter is due to the effect of preferential substitution between Fe and Mn atoms according to TSM.</p>
<p>The reduced magnetization of these alloys deduced from magnetic hyperfine splittings has been correlated with the magnetic transition temperatures in terms of the molecular field theory. It has been found from both the Mössbauer effect and magnetization measurements that for composition 0 ≤ x ˂ 50 both sites I and II are ferromagnetic at liquid-nitrogen temperature and possess moments parallel to each other. In the composition range 50 ˂ x ≤ 100 , the site II is antiferromagnetic whereas site I is paramagnetic even at a temperature below the bulk Néel temperatures. In the vicinity of x = 50 however, site II is in a state of transition between ferromagnetism and antiferromagnetism. The present study also suggests that only Mn in site II are responsible for the antiferromagnetism in Mn<sub>5</sub>Si<sub>3</sub> contrary to a previous report.</p>
<p>Electrical resistance has also been measured as a function of temperature and composition. The resistive anomalies observed in the Mn-rich alloys are believed to result from the effect of the antiferromagnetic Brillouin zone on the mobility of conduction electrons.</p>
|
|---|