Heat treatment effect on wear behaviour of HVOF-sprayed near-nanostructured coatings
No === This study investigates the effect of heat treatment on changes in microstructure and wear behaviour of WC-NiCr coatings. Two feedstock powders with a similar chemical composition and different particle sizes (near nano-structured WC-17NiCr and microstructured WC-15NiCr) were used. High-veloc...
| Main Authors: | , , |
|---|---|
| Language: | en |
| Published: |
2019
|
| Subjects: | |
| Online Access: | http://hdl.handle.net/10454/17079 |
| Summary: | No === This study investigates the effect of heat treatment on changes in microstructure and wear behaviour of WC-NiCr coatings. Two feedstock powders with a similar chemical composition and different particle sizes (near nano-structured WC-17NiCr and microstructured WC-15NiCr) were used. High-velocity oxyfuel spraying technique was used to deposit coatings on to a mild steel substrate using identical spraying parameters. Coated samples were then heat treated in a nitrogen atmosphere at 500 and 700°C. The effect of heat treatment on changes in hardness and wear performance of the coatings was studied using microstructural analysis, micro-hardness indentation and abrasive wear tests. The results showed that the heat treatment increased the hardness of both coatings and a corresponding increase in wear resistance was recorded. The formation of a brittle CrWO4 phase in the microstructured coating resulted in brittle fracture of the coating and this gave lower wear resistance compared to the nanostructured coatings. |
|---|