| LEADER |
01449 am a22001933u 4500 |
| 001 |
6085 |
| 042 |
|
|
|a dc
|
| 100 |
1 |
0 |
|a Tarawneh, Mou'ad A.
|e author
|
| 700 |
1 |
0 |
|a Sahrim Hj. Ahmad,
|e author
|
| 700 |
1 |
0 |
|a Ku Zarina, K.A.
|e author
|
| 700 |
1 |
0 |
|a Ibrahim N. Hassan,
|e author
|
| 700 |
1 |
0 |
|a Yu, Lih Jiun
|e author
|
| 700 |
1 |
0 |
|a Flaifel, Moayad Husein
|e author
|
| 700 |
1 |
0 |
|a Shamsul Bahri, A.R.
|e author
|
| 245 |
0 |
0 |
|a Properties enhancement of TPNR-MWNTs-OMMT hybrid nanocomposites by using ultrasonic treatment
|
| 260 |
|
|
|b Universiti Kebangsaan Malaysia,
|c 2013-04.
|
| 856 |
|
|
|z Get fulltext
|u http://journalarticle.ukm.my/6085/1/11_Mouad.pdf
|
| 520 |
|
|
|a The main goal of this paper was to study the effect of ultrasonic treatment time on the mechanical properties of thermoplastic natural rubber (TPNR) reinforced with hybrid MWNTs-OMMT. The intercalation of TPNR enhancement into layers of clay by increasing the d-spacing was found using X-ray diffraction. The tensile properties of nanocomposites treated with ultrasonic increased when compared with untreated nanocomposites. The optimum ultrasonic treatment time was obtained at 3 h. The transmission electron microscope micrograph showed a combination of intercalated-exfoliated structure of the TPNR composites with organic clay and dispersion of MWNTs. The ultrasonic treatment can promote the dispersion of MWNTs-OMMT in TPNR and also improved the compatibility of hybrid filler and the TPNR matrix.
|