| Summary: | Ultrasonic resonance fatigue test method at 20 kHz related to the very high cycle fatigue (VHCF) aims to accelerate a time-consuming experiment. In this paper, an ultrasonic fatigue device with a data acquisition system was improved for monitoring and recording the data from fatigue tests in which self-heating phenomenon exists. Symmetric tension-compression sinusoidal vibrating mode (<b><i>R</i></b> = −1) was observed in this study. VHCF behavior and mechanism of Inconel 718 were carried out using this device. It was concluded that more than 99% of fatigue life is consumed in initiation duration. Specimen temperature increase was not a decisive factor in VHCF strength for Inconel 718, as long as it was far less than the design temperature limitation. A single initiation site existed at the subsurface facet or grain cluster, observed from scanning electron microscope (SEM) micrographs. Quasi-cleavage fracture in transgranular ductile mode emerged and then tended to trace grain boundaries in an intergranular manner by cleavage-dominated mixed mode.
|
|---|