Evolution of secondary phases in 0.17C-16Cr-11Mn-0.43N austenitic stainless steel at 800 and 850°C: Thermodynamic modeling of phase equilibria and experimental kinetic studies
The precipitation of secondary phases was investigated in the 0.17C-16Cr-11Mn-0.43N austenitic stainless steel during annealing at 800 and 850°C for times between 5 min and 100 h. Light microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy, scanning electron microsco...