1020 AISI-SAE steel Austenitic Nitrocarburising with alcohol and triethanolamine

1020 AISI-SAE steel Austenitic Nitrocarburising with alcohol and triethanolamine

The present work shows AISI-SAE 1020 steel's nitrocarbide layer's microstructure and micro-hardness profile following 4 hours at 700ºC using methanol, isopropanol and triethanolamine. The steel was then hardened by quenching it in water and then tempered at 350ºC for 1 hour. Its surface ha...

Full description

Bibliographic Details
Main Authors: Álvaro Castro P, Carlos Bohórquez
Format: Article
Language:English
Published: Universidad Nacional de Colombia 2005-01-01
Series:Ingeniería e Investigación
Subjects:
thermal treatment
surface treatment
Online Access:https://revistas.unal.edu.co/index.php/ingeinv/article/view/14615
id doaj-fbb7a1e55c3c490fb7cfddb77935fd85
record_format Article
spelling doaj-fbb7a1e55c3c490fb7cfddb77935fd852020-11-25T00:40:29ZengUniversidad Nacional de ColombiaIngeniería e Investigación0120-56092248-87232005-01-01251814135401020 AISI-SAE steel Austenitic Nitrocarburising with alcohol and triethanolamineÁlvaro Castro PCarlos BohórquezThe present work shows AISI-SAE 1020 steel's nitrocarbide layer's microstructure and micro-hardness profile following 4 hours at 700ºC using methanol, isopropanol and triethanolamine. The steel was then hardened by quenching it in water and then tempered at 350ºC for 1 hour. Its surface had been partially oxidised by heating it at 400ºC for 1 hour. An example is given of other researchers analysing microstructure and propierties in steel having 0,5% C, using endothermic gas and different amounts of ammoniac.https://revistas.unal.edu.co/index.php/ingeinv/article/view/14615thermal treatmentsurface treatment
collection DOAJ
language English
format Article
sources DOAJ
author Álvaro Castro P
Carlos Bohórquez
spellingShingle Álvaro Castro P
Carlos Bohórquez
1020 AISI-SAE steel Austenitic Nitrocarburising with alcohol and triethanolamine
Ingeniería e Investigación
thermal treatment
surface treatment
author_facet Álvaro Castro P
Carlos Bohórquez
author_sort Álvaro Castro P
title 1020 AISI-SAE steel Austenitic Nitrocarburising with alcohol and triethanolamine
title_short 1020 AISI-SAE steel Austenitic Nitrocarburising with alcohol and triethanolamine
title_full 1020 AISI-SAE steel Austenitic Nitrocarburising with alcohol and triethanolamine
title_fullStr 1020 AISI-SAE steel Austenitic Nitrocarburising with alcohol and triethanolamine
title_full_unstemmed 1020 AISI-SAE steel Austenitic Nitrocarburising with alcohol and triethanolamine
title_sort 1020 aisi-sae steel austenitic nitrocarburising with alcohol and triethanolamine
publisher Universidad Nacional de Colombia
series Ingeniería e Investigación
issn 0120-5609
2248-8723
publishDate 2005-01-01
description The present work shows AISI-SAE 1020 steel's nitrocarbide layer's microstructure and micro-hardness profile following 4 hours at 700ºC using methanol, isopropanol and triethanolamine. The steel was then hardened by quenching it in water and then tempered at 350ºC for 1 hour. Its surface had been partially oxidised by heating it at 400ºC for 1 hour. An example is given of other researchers analysing microstructure and propierties in steel having 0,5% C, using endothermic gas and different amounts of ammoniac.
topic thermal treatment
surface treatment
url https://revistas.unal.edu.co/index.php/ingeinv/article/view/14615
work_keys_str_mv AT alvarocastrop 1020aisisaesteelausteniticnitrocarburisingwithalcoholandtriethanolamine
AT carlosbohorquez 1020aisisaesteelausteniticnitrocarburisingwithalcoholandtriethanolamine
_version_ 1725289767460929536

Similar Items