The Influence of the Angle of the Working Part of the Die on the High Speed Drawing Process of Low Carbon Steel Wires
The paper contains the theoretical and experimental analysis of the impact of the drawing angle on the drawing process and the properties of low carbon steel wires. A multi-stage drawing wire rod with a diameter of 5.5 mm on a wire with a diameter of 1.0 mm has been carried out in two stages. The fi...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Polish Academy of Sciences
2017-06-01
|
| Series: | Archives of Metallurgy and Materials |
| Subjects: | |
| Online Access: | http://www.degruyter.com/view/j/amm.2017.62.issue-2/amm-2017-0073/amm-2017-0073.xml?format=INT |
| Summary: | The paper contains the theoretical and experimental analysis of the impact of the drawing angle on the drawing process and the properties of low carbon steel wires. A multi-stage drawing wire rod with a diameter of 5.5 mm on a wire with a diameter of 1.0 mm has been carried out in two stages. The first one consisted of preliminary drawing wire rod for the wire with a diameter of 2.2 mm which was next subjected to the drawing process at a speed of 25 m/sec at the final wire with a diameter of 1.0 mm. The wires were drawn in conventional dies with drawing angle α = 3, 4, 5, 6, 7 degrees. |
|---|---|
| ISSN: | 2300-1909 |