| Summary: | The data presented in this article is related to the research experiment, titled: ‘Quasi in-situ energy dispersive X-ray spectroscopy observation of matrix and solute interactions on Y-Ti-O oxide particles in an austenitic stainless steel under 1 MeV Kr2+ high temperature irradiation’ (Brooks et al., 2017) [1]. Quasi in-situ analysis during 1 MeV Kr2+ 520 °C irradiation allowed the same microstructural area to be observed using a transmission electron microscope (TEM), on an oxide dispersion strengthened (ODS) austenitic stainless steel sample. The data presented contains two sets of energy dispersive X-ray spectroscopy (EDX) data collected before and after irradiation to 1.5 displacements-per-atom (~1.25×10−3 dpa/s with 7.5×1014 ions cm−2). The vendor software used to process and output the data is the Bruker Esprit v1.9 suite. The data includes the spectral (counts vs. keV energy) of the quasi in-situ scanned region (512×512 pixels at 56k magnification), along with the EDX scanning parameters. The.raw files from the Bruker Esprit v1.9 output are additionally included along with the.rpl data information files. Furthermore included are the two quasi in-situ HAADF images for visual comparison of the regions before and after irradiation. This in-situ experiment is deemed ‘quasi’ due to the thin foil irradiation taking place at an external TEM facility. We present this data for critical and/or extended analysis from the scientific community, with applications applying to: experimental data correlation, confirmation of results, and as computer based modeling inputs.
|
|---|