| Summary: | The high temperature tensile test of Inconel 718 under the conditions of deformation temperature of 950 °C–1100 °C and strain rate of 0.0005 s<sup>−1</sup>–0.1 s<sup>−1</sup> was carried out, and its true stress–true strain curve was drawn. Through the analysis of the flow stress of Inconel 718 under different conditions, it can be seen that the high-temperature rheological behavior of Inconel 718 is affected by the coupling of strain hardening effect and dynamic softening effect, and has significant loading history correlation. By applying the stretched data, a long short term memory (LSTM) recurrent neural network was trained to characterize the constitutive relationship of Inconel 718. The experimental results show that the prediction results of the LSTM constitutive model are extremely consistent with the experimental data, which is significantly better than the modified Johnson–Cook (M-JC) model. Finally, high temperature tensile experiments under variable strain rates were carried out to verify the feasibility of the LSTM constitutive model in the complex loading and unloading stages.
|
|---|