Observations of corrosion pits and cracks in corrosion fatigue of high strength aluminum alloy by computed-tomography using synchrotron radiation

Observations of corrosion pits and cracks in corrosion fatigue of high strength aluminum alloy by computed-tomography using synchrotron radiation

Measurements of the shape and dimensions of the pits and cracks formed in corrosion fatigue tests of a high-strength aluminium alloy, 7075-T651 were conducted by computed-tomography using ultra bright synchrotron radiation X-ray. Complex corrosion process could be observed and detail shape of cor...

Full description

Bibliographic Details
Main Authors: Shiozawa D., Nakai Y.
Format: Article
Language:English
Published: EDP Sciences 2010-06-01
Series:EPJ Web of Conferences
Online Access:http://dx.doi.org/10.1051/epjconf/20100635004
id doaj-f01ae9ecae1f4c31b069c09c3153cac6
record_format Article
spelling doaj-f01ae9ecae1f4c31b069c09c3153cac62021-08-02T16:17:54ZengEDP SciencesEPJ Web of Conferences2100-014X2010-06-0163500410.1051/epjconf/20100635004Observations of corrosion pits and cracks in corrosion fatigue of high strength aluminum alloy by computed-tomography using synchrotron radiationShiozawa D.Nakai Y.Measurements of the shape and dimensions of the pits and cracks formed in corrosion fatigue tests of a high-strength aluminium alloy, 7075-T651 were conducted by computed-tomography using ultra bright synchrotron radiation X-ray. Complex corrosion process could be observed and detail shape of corrosion pits could be identified. Sometimes, corrosion pit was formed under passive film, and those were not observed from the surface. http://dx.doi.org/10.1051/epjconf/20100635004
collection DOAJ
language English
format Article
sources DOAJ
author Shiozawa D.
Nakai Y.
spellingShingle Shiozawa D.
Nakai Y.
Observations of corrosion pits and cracks in corrosion fatigue of high strength aluminum alloy by computed-tomography using synchrotron radiation
EPJ Web of Conferences
author_facet Shiozawa D.
Nakai Y.
author_sort Shiozawa D.
title Observations of corrosion pits and cracks in corrosion fatigue of high strength aluminum alloy by computed-tomography using synchrotron radiation
title_short Observations of corrosion pits and cracks in corrosion fatigue of high strength aluminum alloy by computed-tomography using synchrotron radiation
title_full Observations of corrosion pits and cracks in corrosion fatigue of high strength aluminum alloy by computed-tomography using synchrotron radiation
title_fullStr Observations of corrosion pits and cracks in corrosion fatigue of high strength aluminum alloy by computed-tomography using synchrotron radiation
title_full_unstemmed Observations of corrosion pits and cracks in corrosion fatigue of high strength aluminum alloy by computed-tomography using synchrotron radiation
title_sort observations of corrosion pits and cracks in corrosion fatigue of high strength aluminum alloy by computed-tomography using synchrotron radiation
publisher EDP Sciences
series EPJ Web of Conferences
issn 2100-014X
publishDate 2010-06-01
description Measurements of the shape and dimensions of the pits and cracks formed in corrosion fatigue tests of a high-strength aluminium alloy, 7075-T651 were conducted by computed-tomography using ultra bright synchrotron radiation X-ray. Complex corrosion process could be observed and detail shape of corrosion pits could be identified. Sometimes, corrosion pit was formed under passive film, and those were not observed from the surface.
url http://dx.doi.org/10.1051/epjconf/20100635004
work_keys_str_mv AT shiozawad observationsofcorrosionpitsandcracksincorrosionfatigueofhighstrengthaluminumalloybycomputedtomographyusingsynchrotronradiation
AT nakaiy observationsofcorrosionpitsandcracksincorrosionfatigueofhighstrengthaluminumalloybycomputedtomographyusingsynchrotronradiation
_version_ 1721229857225965568

Similar Items