Effect of Silicon Content on Wear Behavior of Heat Treated Powder Metallurgy Steels
Three different steel compositions with 1, 3 and 5 mass% Si were prepared using atomized iron (ASC.100.29) and 0.35 mass% natural graphite powders. The mixed powders were cold pressed at 700 MPa and sintered at 1200 °C for 30 min under pure Ar gas atmosphere. Some of the sintered specimens was quenc...