| Summary: | In the presently work ferromagnetic resonance (FMR) of metallic glasses in microwires form of composition (FexCo1-x)72.5 Si12.5 B15 has been measured. The ferromagnetic resonance frequency of amorphous magnetic microwires has been obtained from power absorption measurements in the microwave frequency range. The experimental technique here employed consists on the replacement of the dielectric of a coaxial transmission line by the sample to be measured. From the evolution of the resonance frequency with a dc applied magnetic field, the anisotropy field of the microwires has been deduced, and successfully compared to that obtained from quasi-static hysteresis loops.<br><br>En el presente trabajo se ha medido la frecuencia de resonancia ferromagnética (FMR) de vidrios metálicos en forma de microhilos de composición (FexCo1-x)72.5 Si12.5 B15. Estos microhilos constan de un núcleo magnético de unas 5μm de diámetro y una cobertura de vidrio, siendo el diámetro total de entre 10 y 15 μm según la muestra. La técnica experimental empleada consiste en la sustitución del dieléctrico de una línea de transmisión coaxial por los microhilos a medir, y en la medida de la absorción de potencia a frecuencias de microondas. Para cada muestra se ha ido variando la intensidad de un campo externo de magnetización, provocando la variación de la frecuencia de resonancia. Con estas medidas se ha conseguido establecer la relación entre campo de magnetización y frecuencia de resonancia, y mediante el análisis de los datos obtenidos y contrastados con el modelo teórico propuesto se ha obtenido información del campo de anisotropía de los microhilos. Finalmente, el campo de anisotropía calculado se ha contrastado con el obtenido mediante la medida del ciclo de histéresis quasi-estático.
|
|---|