| Summary: | Alkaline leaching of mechanically activated black dross resulted in an aluminate(III) solution with a small amount of silicate(IV). To obtain pure aluminate(III) solution, the removal of silicate(IV) from the alkaline leaching solution was investigated by adsorption with hydrocalumite (Ca<sub>2</sub>Al(OH)<sub>6</sub>Cl·2H<sub>2</sub>O). The hydrocalumite was synthesized by the coprecipitation method. The characterization of the synthesized hydrocalumite was analyzed via X-ray diffraction (XRD), scanning electron microscopy (SEM) images and Fourier-transform infrared spectroscopy (FTIR). In our experimental conditions, silicate(IV) was selectively adsorbed onto hydrocalumite over aluminate(III). The reaction time greatly affected the removal percentage of aluminate(III) owing to mass action effect. When the reaction time was longer than 2 h, no aluminate(III) was adsorbed onto hydrocalumite and thus it was possible to selectively remove silicate(IV). When the dosage of hydrocalumite was in excess, the removal percentage of silicate(IV) was rather reduced. Complete removal of silicate(IV) from the solution was accomplished in the reaction temperature between 50 and 70 °C. By selective adsorption of silicate(IV) from the solution at the optimum condition (30 g/L hydrocalumite, 50 °C, 400 rpm, and 2 h), an aluminate(III) solution with purity higher than 99.9% was obtained. The adsorption of silicate(IV) onto hydrocalumite followed the Freundlich isotherm.
|
|---|